Abstract:Narrow disperse or monodisperse poly (DVB-co-EGDMA-co-MAA) microspheres with carboxyl groups were prepared by free-radical precipitation polymerization in neat acetonitrile, using 2, 2'-azobisisobutyronitrile (AIBN) as initiator, methylacrylic acid as functional monomer, and highly hydrophobic divinylbenzene-55 (DVB-55) and polarity ethylene glycol dimethacrylate (EGDMA) as mixed crosslinker. The results showed that the feed radio of DVB-55 to EGDMA determined the particle size, size distribution, yield, thermal stability and loading capacity of the functional groups. The particle size of microspheres was in the range of 0.6 similar to 3.8 mu m, and monodisperse microspheres could be obtained when the ratio of DVB-55 to EGDMA was no less than 1:1. Thermogravimetric analysis showed good thermal stability, enhancing with the percentage of DVB-55 in the mixed crosslinker. Moreover, with increasing the amount of DVB-55 in the mixed crosslinker, the measured values of the loading capacity of the accessible carboxylicacid group on the surface of the microspheres decreased,as well as the yield of microspheres. It was confirmed that the composition of the cross-linking monomers affected the particle size, size distribution and yield of microspheres. The studies on the compatibility between the two cross-linkers showed that the core of the polymer beads would contain more DVB units slightly, while the outer layer would contain preferentially the more abundant cross-linker added in the pre-polymerization mixture.

Preparation of Poly (MMA-S-DVB) Microspheres by Suspension Polymerization Method

Preparation of Bicontinuous Porous Polymeric Materials Via Microemulsion Polymerization

Preparation of Micron-sized Monodisperse Poly (Styrene-Co-methyl Methacrylate) Microspheres by Dispersion Copolymerization

Poly(Divinyl Benzene-Co-Ethylene Glycol Dimethacrylate-Co-Methylacrylic Acid) Microspheres Prepared by Precipitation Polymerization

Preparation of Monodisperse Porous St/DVB Copolymer Microspheres

Mini-Emulsification and Mini-Emulsion Polymerization of Methyl Methacrylate/Nanosilica Dipsersion

Preparation and Surface Modification of Magnetic Poly(methyl Methacrylate) Microspheres

Photoinitiated emulsion polymerization of P(MMA-co-DVB) microspheres with low power ultraviolet light

Morphology and blowing agent encapsulation efficiency of vinylidene chloride copolymer microspheres synthesized by suspension polymerization in the presence of a blowing agent

Preparation of Poly (vinyl acetate)Cross-Linked Microspheres with Controllable Size and High Specific Surface Area

Preparation and Characterization of Monodisperse Methyl Methacrylate-Styrene Copolymer Microspheres

Preparation and Characterization of Poly(mma-Egdma-amps) Microspheres by Soap-Free Emulsion Polymerization

Preparation of Poly(methyl Methacrylate-Co-styrene) Microspheres by Dispersion Copolymerization

Study on Preparation and Process of Poly(mma‐st) Thermally Expandablecore‐shellmicrospheres

Synthesis of acrylic resin and methacrylic resin microspheres by suspension polymerization

Preparation of magnetic poly(methylmethacrylate–divinylbenzene–glycidylmethacrylate) microspheres by spraying suspension polymerization and their use for protein adsorption

Study on preparation and process of poly( <scp>MMA‐St</scp> ) thermally expandable <scp>core‐shell</scp> microspheres

Preparation of Thermally Expandable Microspheres by Methyl Methacrylate Suspension Polymerization Assisted with a Foaming Agent

Preparation of Hollow Microspheres by Dispersion Polymerization-Seeded Swelling Polymerization

Preparation and application of cross-linked PVA microspheres with narrow particle size distribution by suspension polymerization using uniform porous tube

Preparation of Surface-Modified Monodisperse Polystyrene Microspheres with Cationic Functional Comonomer