Morphology and microstructure of Yb2O3 layer formed over aluminide coating produced by pack cementation of Haynes® 263 alloy
Jerzy Morgiel,Tomasz Dudziak,Ewa Rząd,Krzysztof Morgiel,Filip Kateusz
DOI: https://doi.org/10.1007/s43452-024-00869-x
IF: 4.042
2024-02-13
Archives of Civil and Mechanical Engineering
Abstract:Intermetallic coatings from the Ni–Al system modified with rare earth elements (REE) additions are developed to protect the Ni-based superalloys against the increasingly demanding operating conditions, like those at ultra-supercritical (A-USC) power plants. The pack cementation process is generally limited to treatment of smaller parts, but simultaneously it allows to produce thick, well adhering and easily alloyed coatings. In this experiment, the Haynes ® 263 alloy was subjected to pack cementation (PC) aluminizing process. The powder bed used in this experiment was prepared in two stages, i.e., first, the Al (8 wt.%), AlCl 3 (4 wt.%), and Al 2 O 3 (88 wt.%) powders were thoroughly mixed and only then, the Yb (1.5 wt.% of the all former) was added. The coating obtained through this process was investigated using scanning and transmission electron microscopy (SEM/TEM) methods. It helped to prove that the diffusive layer consisted mostly of Al 14 Cr 3 Ni 2 ζ-phase, with significant amount of Al 13 (Co, Cr) 4 and (Ni, Co, Cr) 3 Al 4 larger precipitates as well as numerous smaller ones, composed of (Al, Ni, Co, Cr, Ti) or (Al, Ni, Co, Cr, Mo). The additive layer consisting of Al 3 Ni 2 phase with up to 6 at. % Co and 2 at. % Cr was covered by a discontinuous layer of α-Al 2 O 3 occasionally decorated with particles of the same phase. Only the very surface was found to be occupied by an amorphous Yb 2 O 3 oxide, which formed a thin (~ 5 nm), but simultaneously a continuous layer. The latter finding is the first experimental documentation of the location of REE in the coating obtained through PC process using a powder bed modified with elements from that group.
engineering, mechanical,materials science, multidisciplinary, civil