Abstract:The research was mainly focused on the phase transformation of Ti-42Al-5Mn (at%) alloy produced by vacuum induction melting (VIM) and vacuum arc remelting (VAR) followed by wrought process. The phase transformation kinetics of the alloy during continuous cooling under the cooling rates of 0.1 degrees C/s, 0.5 degrees C/s, 2 degrees C/s, 10 degrees C/ s, 50 degrees C/s, and 200 degrees C/s were identified by the Gleeble-3800 system, which is finally used to construct a schematic continuous cooling transformation (CCT) diagram of this alloy. The related phase composition, microstructure and property of the alloy were studied using X-ray diffraction (XRD), electron probe micro analyzer (EPMA), transmission electron microscope (TEM) and Vickers hardness (HV). It shows that six kinds of phase transformation are existed during continuous cooling from 1300 degrees C with the cooling rates of 0.1 degrees C/s, 0.5 degrees C/s, 2 degrees C/s, 10 degrees C/s, 50 degrees C/s, 200 degrees C/s and WQ, including beta ->alpha(2)', beta ->alpha, beta ->gamma, beta ->beta(o)/alpha ->alpha(2), alpha(2)->alpha(2)/gamma and alpha(2)/gamma ->beta(o,sec).It reveals that partial transformations would be inhibited when the cooling rate is relatively high. The martensitic structures (alpha(2)') obtained by beta ->alpha(2) were formed under the WQ condition after holding at 1300 degrees C for 5min, and it will be completely restrained below the cooling rate of WQ. For the beta ->gamma, it is restrained if the cooling rates are higher than 50 degrees C/s. The alpha(2)->alpha(2)/gamma could be also suppressed when cooling with 200 degrees C/s, and the gamma lath within the supersaturated alpha(2)-grains would be formed at lower cooling rate below 50 degrees C/s. For 0.5 degrees C/s and 0.1 degrees C/s, a small amount of dotted beta(o) (beta(o,sec)) phases can be formed in the lamellar interfaces, which is proved the reaction products of alpha(2)/gamma ->beta(o,sec). Furthermore, the effect of cooling rates on the microstructure, including interlamellar spacing (lambda) and gamma grains are also identified and discussed.

Measurement for Phase Transformation Point of Ti80 Alloy

Size Dependent Phase Transformation in Atomized TiAl Powders

Determination of Phase Transformation Point of TC21 Titanium Alloy

Measurement and Analysis of Phase Transformation Temperature of TC1l Titanium Alloy

Investigation of the Phase Transformations in Ti 22al 25nb Alloy

Effect of Cooling Rate on Phase Transformation in Ti2AlNb Alloy

Phase Transformation Behavior of a Β-Solidifying Γ-Tial-based Alloy from Different Phase Regions with Various Cooling Methods

Influence of Ti on Solid Microstructure and Phase Transformation of Cu75Cr25 Alloy at Different Cooling Conditions

Study on Behaviors of Annealed Microstructure and Hardness Development in AlFeCuCoNiCrTix High-entropy Alloys

Phase Transformation During Continuous Heating in a Β-Quenched Ti-5Al-3Mo-3V-2Cr-2Zr-1Nb-1Fe Alloy

Phase Transformations of the L1 2 -Ti 3 Al Phase in Γ-Tial Alloy

The Crystal Structure, Microhardness and Thermal Stability of the Ti26Al55Zn19 Alloy

The phase transformation during the low temperature aging and low rate heating process of metastable titanium alloys

Characterization of (α+β)/β Transformation in a TC11 Titanium Alloy

Phase Particle Coarsening Dynamics and Pattern Change in Ti-6Al-4V Alloy

Phase transformation and microstructure of quaternary TiNiHfCu high temperature shape memory alloys

Study on the Transformation of (α+β) Phase to Β Phase in Deformed Ti-6Al-4V Alloy During the Heat Treatment

Insitu Study Of Phase-Transformations In A 50.8 At-Percent Ni-Ti Alloy

Phase Transformation Behavior of Ti49ni49.5fe1v0.5 and Ti48ni48.5fe1v2.5 Alloys after Different Heat Treatments

TiC phase in Ti alloys at different temperatures

Phase Transformation Behavior of a Mn Containing Β-Solidifying Γ-Tial Alloy During Continuous Cooling