Influence of Thermal Treatment on Element Partitioning in Α+β Titanium Alloy
Sensen Huang,Jinhu Zhang,Yingjie Ma,Shilin Zhang,Sabry S. Youssef,Min Qi,Hao Wang,Jianke Qiu,Dongsheng Xu,Jiafeng Lei,Rui Yang
DOI: https://doi.org/10.1016/j.jallcom.2019.03.332
IF: 6.2
2019-01-01
Journal of Alloys and Compounds
Abstract:The partitioning of alloying elements during the α+β solution treatment, accompanying the α↔β phase transformation, determines the composition and stability of the microstructure, and thus significantly influences the ultimate mechanical behavior of α+β titanium alloys. In the current study, the influence of two main factors, i.e., the solution temperature and the isothermal solution time, on element partitioning in Ti6Al4V alloy was investigated. The distribution of alloy elements in both phases was quantitatively analyzed by the electron probe micro-analyzer (EPMA). The results indicated that, with the increase of the solution temperature, an evident change in composition occurred in the β transformed structure (βt), while the composition in the primary α phase (αp) remained almost constant, because of the higher atomic mobilities in the β phase than in the α. With longer solution time, there appeared a steeper composition gradient and a smaller transition range of element concentration around the αp/βt boundary. Phase field simulation revealed the evolution of microstructure and composition toward equilibrium at a constant solution temperature and verified the above experimental results from the perspective of elemental diffusion and kinetics.