Dynamic recrystallization behavior of β grains in hot deformed Ti-6Mo-5 V-3Al-2Fe alloy

Lin Han,Haoyu Zhang,Chuan Wang,Ge Zhou,Siqian Zhang,Lijia Chen
DOI: https://doi.org/10.1007/s00170-023-11165-y
IF: 3.563
2023-02-28
The International Journal of Advanced Manufacturing Technology
Abstract:High temperature compression tests were carried out on Ti-6Mo-5 V-3Al-2Fe alloy. EBSD and TEM analysis were performed on α + β phase and β phase to study the microstructure and dynamic recrystallization mechanism. The results show that the dynamic recrystallization of the alloy is difficult to occur during hot deformation in the α + β phase region because of the existence of α phase. A little amount of dynamic recrystallizated β grains can be formed when the deformation temperature is below β-transus. When the deformation temperature is 760 °C, and the strain rate is greater than 0.005 s–1, the recrystallized grains are formed along the primary β grain boundary under the influence of discontinuous dynamic recrystallization mechanism, and the primary β grains are not significantly refined. When the deformation temperature is 710 ℃ and 760 ℃, the average β grain size is the smallest at the strain rate of 0.05 s–1. When the deformation temperature is above β-transus, the dynamic recrystallization can occur relatively easy, and a large amount of dynamic recrystallizated β grains can be observed. When the deformation temperature is 810 ℃ and the strain rate is 0.005 s–1, the β grains exhibit the smallest size difference and the minimum average size of 20.53 μm. The recrystallization mechanism of the alloy is the mixed behavior of continuous dynamic recrystallization and discontinuous dynamic recrystallization.
engineering, manufacturing,automation & control systems
What problem does this paper attempt to address?