Phase transformation from η phase to S phase at grain boundary during annealing in rapidly-solidified Al-Zn-Mg-Cu alloy
Zhiping Wang,Jiwei Geng,Peikang Xia,Yugang Li,Wei Chen,Xianfeng Li,Mingliang Wang,Dong Chen,Haowei Wang
DOI: https://doi.org/10.1016/j.matchar.2022.112531
IF: 4.537
2022-12-02
Materials Characterization
Abstract:Phase transformation during annealing in rapidly-solidified Al-Zn-Mg-Cu alloy was investigated by differential scanning calorimetry, X-ray diffraction, transmission electron microscopy and transmission Kikuchi diffraction technologies. The results show that primary η-Mg(Zn,Al,Cu) 2 phase is formed at grain boundaries and inside grains during spray forming. During annealing above 300 °C, the primary η phase particles at GBs are inclined to be decomposed as newly-oriented nano η phase particles via lattice rotation at η/Al interface and directly transformed to S-(Al 2 CuMg) phase while those inside grains are directly dissolved. Nanoscale crystallographic orientation relationships between newly-formed η phase and transformed S phase at η/Al interface are revealed. Due to the phase transformation from η to S, the impact toughness of Al-Zn-Mg-Cu alloy is significantly deteriorated because these S phase particles cannot be fully dissolved by solution treatment and inevitably increase brittle fracture sensibility. This finding provides new insights into designing the phase transformation in Al-Zn-Mg-Cu alloys for toughness enhancement.
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing