Crystallographically Textured Zn2W-type Barium Hexaferrite for Microwave and Millimeter Wave Applications
Yu Wang,Yingli Liu,Xin You,Shiheng Liu,Chongsheng Wu,Qian Liu,Huaiwu Zhang,Vincent G. Harris
DOI: https://doi.org/10.1016/j.jallcom.2018.09.087
IF: 6.2
2018-01-01
Journal of Alloys and Compounds
Abstract:Crystallographically c-axis textured Zn2W barium ferrites (i.e., BaMe2Fe16O27), synthesized by traditional ceramic methods, are presented as a high-magnetic-remanence material for self-biased microwave and millimeter wave applications. A magnetic field orientation process was applied to obtain c-axis texture of ferrite materials while sintering parameters were systematically optimized to obtain high-performance materials for self-biased circulators and isolators. X-ray diffraction (XRD) and scanning electron microscopy (SEM) were used to confirm structure, crystal orientation, and microstructural morphology of the Zn2W ferrite final product. Room temperature vibrating-sample magnetometry (VSM) was applied to measure hysteresis (M vs. H) loops that provided an evaluation of coercivity (Hc), magnetization (M), and magnetic remanence (Mr) and squareness ratio (Mr/Ms). The ferrite samples sintered at 1020 degrees C demonstrated excellent magnetic properties, such as high squareness ratio (similar to 0.8), relative density (89% of theoretical), 4 pi M-S similar to 3115 Gauss, and coercive fields of similar to 1011 Oe. (C) 2018 Elsevier B.V. All rights reserved.