Abstract:M-type barium ferrite powders doped with Zr4+ ions (BaFe12-xZrxO19 x = 0-0.4), possessing high permittivity and multi-resonant permeability, were synthesized by the sol-gel process. The single-phase hexagonal plate-like barium ferrites were formed with Zr4+ substituting Fe3+ at the 4f(1) sites initially and then at the 2b sites afterwards with increasing doping content. The H-a of the ferrites decreased from 15.75 kOe to 8.13 kOe with increasing Zr4+ from x = 0 to 0.4. The epsilon' and epsilon" of the ferrite with Zr4+ doping were increased to 7.7-6 and 3.4-1.5 over 18-40 GHz from 5.8-5 and 0.7-0.4 without doping, respectively. Contributed mainly by the enhanced permittivity, the matching thicknesses of the Zr4+ ions doped ferrites were as low as only similar to 1 mm or below, i.e. 1.5-3 times thinner than those reported recently. The complex permittivity was still close to the complex permeability in the doped ferrites. Hence, a strong reflection loss of similar to-50 dB could be attained and the absorptivity of electromagnetic (EM) power per unit thickness reached as high as 0.156% mu m(-1), i.e. 2-5 times higher than those of novel absorbing materials. The multi-resonance permeability peaks originated from Fe3+ ions, and exchange couplings among Fe3+, Fe2+ and O- contributed multiple reflection loss peaks and thus, a broad bandwidth of similar to 12 GHz (RL < -10 dB), which was 2-4 times broader than those normally reported. Consequently, the Zr4+-doped barium ferrites are promising for use as excellent absorbing materials in the millimeter wavelength frequency range.

The Synthesis, Characterization and Microwave Properties of ZnCo-Substituted W-Type Barium Hexaferrite, from a Sol-Gel Precursor

The tunable microwave absorption properties of the Co2+–Zr4+ co-substituted Co2W-type hexagonal ferrites

Research on Microwave Properties of Fe-poor W-type BaZnxCO2-xFe15.5O27 Ferrite

Effect of Divalent Metal Ions Substitution on the Magnetic Properties of Ba3Co2-Me Fe24O41 (me = Zn2+, Ni2+) Hexagonal Ferrites

A Study of Structural, Magnetic and Various Dielectric Parameters of Ca-Substituted W-Type Hexaferrites for Applications at 1–6 GHz Frequencies

Microwave absorption studies of W-hexaferrite prepared by co-precipitation/mechanical milling

Effects of Zn substitution on high-frequency properties of Ba<sub>1.5</sub>Sr<sub>1.5</sub>Co<sub>2-x</sub>ZnxFe<sub>22</sub>O<sub> 41</sub> hexaferrites

Effects of Zn substitution on high-frequency properties of Ba1.5Sr1.5Co2-xZnxFe22O41 hexaferrites

Structures and high-frequency magnetic properties of CoZn-X tvpe barium hexaferrites

Preparation and excellent microwave absorption performance of Eu-substituted Ba3Co2-Eu Fe24O41 hexaferrites with multilayer nanoplates stacked and thickened along the c-axis

Magnetic Resonance Behavior Modulation of Ba3Co1.6-xZnxCu0.4Fe24O41 Hexaferrites for Microwave Absorption and Surface Wave Suppression

Preparation and Magnetic Characterization of Y-Type Hexaferrites Containing Zinc, Cobalt-And Copper

Preparation and Magnetic Properties of BaZn2−xCoxFe16O27 Nanocrystalline Powders by the Stearic Acid Gel Method

Influence of Sr2+ Doping Quantity on Microstructure and Magnetic Performance of Z Type Hexagonal Ferrite

Zr4+ Doping-Controlled Permittivity and Permeability of Bafe12-Xzrxo19 and the Extraordinary Em Absorption Power in the Millimeter Wavelength Frequency Range

Microstructure and Properties of Co 2 Z Hexaferrite Prepared by Gel Self-Propagating Method

The Effect of Zn Ion Substitution on Electromagnetic Properties of Low-Temperature Fired Z-type Hexaferrite

Dielectric Behavior and DC Resistivity of Ba3Co2(1−X)Cu2XFe24O41(Co2Z)Hexaferrite

Dielectric behavior and DC resistivity of Ba3Co2(l-X)Cu2XFe24O41 (Co(2)Z)hexaferrite

High-frequency magnetic and dielectric properties of Ba1.5Sr1.5Co1Zn1Fe23O41 hexaferrites with Bi2O3 additives

Synthesis and characterization of BaZn2−xMgxFe16O27 (x = 0.0, 0.5, 1.0, 1.5 and 2.0) hexaferrites for high-frequency antenna application