Looking Into How Nickel Doping Affects the Structure, Morphology, and Optical Properties of TiO 2 Nanofibers
Sanita Ahmetović,Zorka Ž. Vasiljević,Jugoslav B. Krstić,Matjaž Finšgar,Dmytro Solonenko,Dragana Bartolić,Nenad B. Tadić,Goran Miskovic,Nikola Cvijetićanin,Maria Vesna Nikolic
DOI: https://doi.org/10.1016/j.surfin.2024.104434
IF: 6.2
2024-05-04
Surfaces and Interfaces
Abstract:In this paper, we have systematically studied the structural, morphological, and optical properties of Ni-doped TiO 2 , synthesized via a simple, cost-effective electrospinning method followed by calcination at 500 °C. The nanofibers with a core-shell structure were relatively homogeneous, smooth and randomly oriented, and there were no significant differences in fiber diameters due to Ni 2+ content. Core loss mapping using electron energy loss spectroscopy confirmed an even distribution of titanium and relatively uniform nickel in the fibers. It was found that doping with 0.5 mol.% Ni 2+ decreased the rutile content, while doping with 1 mol.% Ni 2+ resulted in a pure anatase phase with a significantly increased specific surface area (36.6 m 2 /g). Further increase in Ni 2+ content (3-10 mol.%) not only prolonged the response of TiO 2 nanofibers to visible light, but also increased the specific surface area (49.5 m 2 /g), decreased crystallite size (7 nm), and increased rutile content in TiO 2 (33 wt.%). Photoluminescence analysis revealed that doping TiO 2 with different amounts of Ni 2+ leads to a gradual decrease of emission spectra intensity and red shift in the maxima positions. The XPS results confirmed that as the Ni 2+ content enlarged, the Ti 2+ and Ti 3+ content increased significantly, effectively promoting the formation of oxygen vacancies. Raman analysis showed that an increase in nickel content (3-5 mol.%) led to a decrease and shift in peak intensity due to Ti 3+ formation and also the possible presence of NiTiO 3 phases. HRTEM analysis showed that Ni was doped into the substitution sites of both the anatase and rutile TiO 2 lattice but had a stronger influence on the distortion of the anatase phase. The photocatalytic activity of Ni-doped TiO 2 nanofibers was explored by analyzing the degradation of an antibiotic, oxytetracycline, monitored in laboratory conditions under visible light irradiation. After 60 minutes of irradiation, the degradation of OTC with 1Ni-TiO 2 reached 76.4% and with 10Ni-TiO 2 70.5%.
chemistry, physical,physics, applied, condensed matter,materials science, coatings & films