Microstructure, shear strength and dielectric properties of a co-fired YIG-MCT composite substrate for circulators
Wenjing Zhao,Fu Wang,Jingsong Liu,Lijia Cao,Xu Huang,Fei Yang,Chong Xian,Honglan Yuan
DOI: https://doi.org/10.1016/j.ceramint.2022.01.031
IF: 5.532
2022-04-01
Ceramics International
Abstract:A YIG-MCT composite substrate for circulators with high shear strength and good dielectric properties was prepared by direct co-firing. The Bi0.3Y2.3Ca0.4Zr0.4Fe4.6O12 (B-YIG) ceramic acted as the inner core, and the 0.95MgTiO3-0.05CaTiO3 (95MCT) ceramic acted as the outer ring of the co-fired composite substrate. The influence of co-firing temperatures on the phase composition, microstructure, shear strength and dielectric properties of the as-prepared composite substrate was investigated. Moreover, the transition region of the composite substrate, induced by direct cosintering, was deduced. The results show that the optimal co-firing temperature of the composite substrate is 1280 °C. At the co-firing temperature, the obtained composite substrate shows a high shear strength of 64.20 MPa. New phases, such as MgFe2O4, Y2Ti2O7, and YFeO3, form in the transition region because of the interface reaction occurring between B-YIG and 95MCT. The synthesized YIG-MCT composite substrate shows a dielectric constant of 19.7 and a dielectric loss of 5.64 × 10−4 (9 GHz), demonstrating good dielectric properties. The results indicate that YIG-MCT prepared by co-firing technology is a promising composite substrate for circulator applications.
materials science, ceramics