Anisotropic Vortex-Flux Rotation in Grain-Orientedyba2cu3

Liwen Liu,J. S. Kouvel,T. O. Brun

DOI: https://doi.org/10.1103/physrevb.46.14113

1992-01-01

Abstract:Magnetization-vector measurements were made at 4.2 K on a grain-oriented ${\mathrm{YBa}}_{2}$${\mathrm{Cu}}_{3}$${\mathrm{O}}_{7}$ sample rotated in the fixed external field ${\mathbf{H}}_{\mathit{e}}$ that was initially applied in the a-b plane or along the c axis during cooling from above ${\mathit{T}}_{\mathit{c}}$. The penetrating vortex-flux component of the sample magnetization was determined as a vector (${\mathbf{M}}_{\mathit{P}}$) over a complete rotational cycle, with diamagnetic shielding and demagnetization effects taken into account. At low ${\mathit{H}}_{\mathit{e}}$, ${\mathbf{M}}_{\mathit{P}}$ turns rigidly with the rotating sample, and this simple behavior persists up to ${\mathit{H}}_{\mathit{e}}$=1 kOe when applied along c during cooling. However, for ${\mathit{H}}_{\mathit{e}}$=1 kOe applied along a-b during cooling, ${\mathbf{M}}_{\mathit{P}}$ reverses its direction in the a-b plane periodically, while its magnitude varies roughly as the projection of ${\mathbf{H}}_{\mathit{e}}$ on a-b. At higher ${\mathit{H}}_{\mathit{e}}$ (\ensuremath{\ge}3 kOe), the rotational behavior of ${\mathbf{M}}_{\mathit{P}}$ is the same for both field-cooling directions. One part of ${\mathbf{M}}_{\mathit{P}}$ continues to show a periodic vortex motion in and out of the a-b plane, while another part stays fixed in direction relative to ${\mathbf{H}}_{\mathit{e}}$ and thus turns frictionally relative to the rotating sample. The observed properties testify to a pronounced anisotropy of the vortex pinning forces, but many of their detailed features, including those that reveal a vortex cross-flux effect, are not yet clearly understood.