Vortex-Flux Rotation In Polycrystalline Yba2cu3o7 At 77-K

liwen liu,j s kouvel,torben o brun

DOI: https://doi.org/10.1063/1.350168

IF: 2.877

1991-01-01

Journal of Applied Physics

Abstract:Magnetization-vector measurements at 77 K on a field-cooled sample rotated by angle-theta relative to fixed field H reveal that M(p), the penetrating vortex-flux component of the magnetization, undergoes some extraordinary changes at H almost-equal-to 30 Oe. As theta is raised above 180-degrees, M(p) decreases in size to a very small minimum while its direction shifts rapidly, and these changes repeat as theta is then lowered below 180-degrees. This behavior, which evolves systematically with H, was observed earlier for the same sample at 4.2 K but at much higher H (approximately 800 Oe) and is readily ascribed to a broad distribution in strength of the vortex pinning forces. Due to this distribution, the vortex lines bifurcate into two groups, one of which rotates rigidly with the sample while the other is held by H and turns frictionally relative to the sample.