Effects of Si variation and Zr addition on the microstructure, oxidation resistance and mechanical property at 1523 K of Nb-Si-Ti/Zr/Hf-Cr/Al high-entropy superalloys
Zijun Fan,Ben Niu,Qing Wang,Jianjun Sha,Chuang Dong
DOI: https://doi.org/10.1016/j.jallcom.2023.169304
IF: 6.2
2023-02-19
Journal of Alloys and Compounds
Abstract:The present work investigated the influences of the variation of Si content and the minor amount of Zr addition on the microstructure, oxidation resistance and mechanical property at 1523 K of Nb-Si-Ti/Zr/Hf-Cr/Al high-entropy superalloys systematically. Alloy compositions with Nb-21.6(Ti/Zr)-3.1Hf-(9.4–15.6)Si-6.3Cr-3.1Al-1.0B (at. %) were designed using a cluster formula approach to realize the substitution of similar elements, in which these alloys were solid-solutionized at 1573 K for 24 h and then aged at 1273 K for 24 h. It was found that all these aged alloys are mainly composed of BCC-Nb solid solution (Nbss), Nb 5 Si 3 and Cr 2 Nb phases, where the increase of Si content and the addition of Zr could significantly increase the volume fraction of Nb 5 Si 3 in a form of coarse and primary particles. Consequently, high-Si alloys possess outstanding mechanical property at high temperature, as evidenced by the fact that the yield strength ( σ YS = 373 MPa) at 1523 K of high-Si/Zr alloy containing 15.6 at. % Si and 1.6 at. % Zr is much higher than that ( σ YS = 266 MPa) of the low-Si alloy with 9.4 at. % Si and 0 Zr. It is mainly ascribed to the existence of primary Nb 5 Si 3 particles, besides the eutectic microstructure composed of Nbss and Nb 5 Si 3 , as well as fine Cr 2 Nb precipitates in Nbss. Moreover, a minor amount of Zr substitution for the Ti is conducive to the phase transition of α-Nb 5 Si 3 to γ-Nb 5 Si 3 . Thus, this high-Si/Zr alloy exhibits an improved oxidation resistance after 50 h-exposure at 1523 K, due to the lowest mass gain of about 80.9 mg/cm 2 . The constitutions of oxide scales in these alloys were characterized and compared, from which it was found that the better oxidation resistance is closely related to the formation of dense oxide scales. This work will provide a new approach to obtain an optimum combination of mechanical property and oxidation resistance of superalloys through multi-component alloying.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering