Normal-state Spin Gap of Bi-based Superconductors

Zhiqiang Mao,Gaojie Xu,Ruiping Wang,Keqing Wang,Mei Tian,Yuheng Zhang

DOI: https://doi.org/10.1103/physrevb.55.14581

1997-01-01

Abstract:The thermoelectric power (TEP) S(T) and resistivity \ensuremath{\rho}(T) were measured for underdoped and overdoped ${\mathrm{Bi}}_{1.8}$${\mathrm{Pb}}_{0.2}$${\mathrm{Sr}}_{2}$${\mathrm{Ca}}_{\mathrm{n}\mathrm{\ensuremath{-}}1}$${\mathrm{Cu}}_{\mathrm{n}}$${\mathrm{O}}_{2\mathrm{n}+4+\mathrm{\ensuremath{\delta}}}$ (n=1,2) samples with different oxygen contents. A specific heat measurement was also conducted for the n=2 system. We found that S(T) exhibited a significant enhancement below a characteristic temperature ${\mathrm{T}}_{\mathrm{g}}$ for these samples, as observed in underdoped samples of ${\mathrm{YBa}}_{2}$${\mathrm{Cu}}_{3}$${\mathrm{O}}_{7\mathrm{\ensuremath{-}}\mathrm{\ensuremath{\delta}}}$ and ${\mathrm{YBa}}_{2}$${\mathrm{Cu}}_{4}$${\mathrm{O}}_{8}$. Such an anomaly in S(T) below ${\mathrm{T}}_{\mathrm{g}}$ suggests that an energy gap exists in the normal states of underdoped and overdoped Bi-based superconductors (n=1 or 2). The normal-state gap temperature (${\mathrm{T}}_{\mathrm{g}}$) increases with decreasing oxygen content in both n=1 and 2 systems. A downturn behavior in \ensuremath{\rho}(T) with the opening of a normal-state gap was also observed for some overdoped samples. On the other hand, the experimental data also showed that S(T) had a positive slope at high temperatures for the heavily overdoped samples of the n=1 system, while all the overdoped samples of the n=2 system had a negative slope in S(T) within the whole measured temperature range. This suggests that the ${\mathrm{Bi}}_{2}$${\mathrm{O}}_{2}$ layers are metallic and make a contribution to the TEP in the heavily overdoped region of the n=1 system, but are insulating in the whole overdoped region of the n=2 system. In addition, specific heat measurements for the n=2 system reveal that a decrease in oxygen content results in the occurrence of phase segregation.