Abstract:Thermally-induced cracking typically occurs during the cooling stage of various manufacturing processes, and is commonly seen in multiphase or the joints of dissimilar materials due to mismatch in their thermo-mechanical properties, such as thermal expansion, elastic-plastic deformation and, in some cases, phase transformation. However, the underlying cracking mechanism associated with local microstructure is still elusive. To improve the mechanistic understanding of thermal cracking, this work uses the diffusion-bonded 9Cr-1Mo steel as an example to study the key microstructural variables, such as interfacial phases, voids, grain boundary migration and crystallographic orientations. Meanwhile, a temperature-dependent crystal plasticity model coupled with a cohesive zone model is developed to provide more insights into the thermal-induced stress distribution at the grain scale. It is found that the stress at the void-free boundary of martensite and ferrite is dominated by shear, and its magnitude is insufficient to nucleate cracks. Whereas voids at phase boundaries can induce significant tensile stress, resulting in cracking at the phase boundaries as well as diffusion-bonded interfaces. Also, the occurrence of interfacial grain boundary migration plays an important role in local stress distribution. These microstructure features and their evolution are experimentally observed and used to verify the developed crystal plasticity models. These findings enhance the understanding of the influence of microstructure features on thermal cracking and provide a guide to designing and fabricating the microstructure with improved thermal crack resistance in various manufacturing processes.

DISCOVERY OF INNER CRACK RECOVERY AND ITS STRUCTURE CHANGE IN 20mnmo STEEL

Internal Crack Recovery of 20mnmo Steel

Microstructure and mechanical properties of internal crack healing in a low carbon steel

Self-healing Mechanism of Inner Crack in Plastic Deformation under High Temperature

Evolution Behaviors and Mechanisms of Internal Crack Healing in Steels at Elevated Temperatures

Cracking in a Fe–25Mn–3Si–3Al Steel

Principle of Internal Defects Recovery in Processes of High Temperature Plastic Deformation

Restoration of Impact Properties of Internal Crack Healing in A Low Carbon Steel

Crack Healing And Mechanical Properties Recovery In Sa 508-3 Steel

Inner crack with inclusion and forging process control of heavy forgings

A novel crack healing technique in a low carbon steel by cyclic phase transformation heat treatment: The process and mechanism

Morphological Evolution During Diffusive Healing of Internal Cracks Within Grains of Α-Iron

Diffusive Healing of Transgranular Fatigue Microcracks Within Alpha-Iron

Effect of deformation modes and heat treatment on microstructure and impact property restoration of internal crack healing in SA 508 steel

Effect of Heat Treatment on Microstructure and Hardness of Internal Crack Healing in a Low Carbon Steel

In-situ three-dimensional X-ray investigation on micro ductile fracture mechanism of a high-Mn steel with delayed necking effect

Strain Visualization of Growing Short Fatigue Cracks in the Heat-Affected Zone of a Ni–Cr–Mo–V Steel Welded Joint: Intergranular Cracking and Crack Closure

MORPHOLOGICAL EVOLUTION OF INTERNAL FATIGUE MICROCRACKS IN Α-Iron DURING DIFFUSIVE HEALING

Effect of Microstructure on Appearance of Near-Threshold Fatigue Fracture in Cr–Mo–V Steel

Thermal cracking: clarifying the effects of phases, voids and grains through characterisation and crystal plasticity modelling

Thermal Mechanical Behavior and Microstructure Characteristics of As‐Cast FeCrNiAl Steel