Dense La0.3Sr0.7TiO3 Interconnect Sintered in Air Atmosphere at a Reduced Temperature with Improved Conductivity for Solid Oxide Electrochemical Cells

Juan Xie,Fang-Ze Han,Jing-Hui Zhang,Sheng Liu,Yu-Hua Tang,Cheng-Xin Li,Shan-Lin Zhang

DOI: https://doi.org/10.1016/j.jeurceramsoc.2023.12.082

IF: 5.7

2024-01-01

Journal of the European Ceramic Society

Abstract:La-doped SrTiO3 (LaxSr1-xTiO3, LST), as the promising ceramic-based interconnect material, usually needs to be sintered in reductive atmosphere at a temperature >= 1450 degrees C, such sintering condition is not friendly to cell fabrication and application. To reduce the sintering temperature of air-sintered LST, seven sintering additives, Bi2O3, Fe2O3, Li2O, MnO2, NiO, V2O5, and Co3O4, are added to the LST in this work. The results show that only Co3O4 is conductive to remarkable sintering at the temperatures of 1250 degrees C. The relative density of LST-3%Co3O4 reaches 92%, while that of the pure LST is only 48%. Moreover, the conductivity of LST-3%Co3O4 achieves 8.2 S/ cm at 800 degrees C in humidified hydrogen, which exceed 5.5 times that of the pure LST. Interestingly, LST-3%Co3O4 exhibits an average TEC of 11.5 x 10-6 K-1 between 400 and 900 degrees C, which is very close to that of other components of SOCs.