Li4Zn(PO4)2:Mn2+ thermosensitive phosphor with dual luminescent centres for optical thermometry

Jie Li,Jie Fu,Jianhua Lin,Yanling Chen,Yinuo Wen,Mingxiao Han,Shuyang Chen,Degang Deng

DOI: https://doi.org/10.1002/bio.4692

IF: 2.613

2024-02-22

Luminescence

Abstract:A Mn2+‐doped Li4Zn(PO4)2:Mn2+ sample with dual‐band emission was successfully synthesized, revealing two distinct emissions originating from four‐coordinated Zn sites and six‐coordinated interstitial sites. Notably, as the temperature was varied, the luminescence centres demonstrated disparate temperature dependencies. Calculated based on fluorescence intensity ratio technology, the Sa and Sr values at 483 K were determined to be 1.69% K−1 and 0.12% K−1, respectively. An optical thermometry strategy based on Mn2+‐doped dual‐wavelength emission phosphor has been reported. Samples with different doping content were synthesized through a high‐temperature solid‐phase method under an air atmosphere. The electronic structure of Li4Zn(PO4)2 was calculated using density functional theory, revealing it to be a direct band gap material with an energy gap of 4.708 eV. Moreover, the emitting bands of Mn2+ at 530 and 640 nm can be simultaneously observed when using 417 nm as the exciting wavelength. This is due to the occupation of Mn2+ at the Zn2+ site and the interstitial site. Further analysis was conducted on the temperature‐dependent emission characteristics of the sample in the range 293–483 K. Mn2+ has different responses to temperature at different doping sites in Li4Zn(PO4)2. Based on the calculations using the fluorescence intensity ratio technique, the maximum relative sensitivity at a temperature of 483 K was determined to be 1.69% K−1, while the absolute sensitivity was found to be 0.12% K−1. The results showed that the Li4Zn(PO4)2:Mn2+ phosphor has potential application in optical thermometry.

chemistry, analytical