Bifunctional Optical Probe Based on La 3 Mg 2 SbO 9:Mn 4+phosphors for Temperature and Pressure Sensing

Zhanglin Chen,Songmo Du,Fei Li,Shijia Zhang,Shuo Zhao,Zhaobo Tian,Jie Zhang,Xuanyi Yuan,Guanghua Liu,Kexin Chen

DOI: https://doi.org/10.1016/j.jmst.2023.12.074

2024-01-01

Abstract:Photoluminescent materials, serving as optical probes, constitute a significant medium for reliable remote sensing of fundamental state parameters such as temperature and pressure. Herein, we report a novel Mn 4 + -activated perovskite-type La 3 Mg 2 SbO 9 phosphor (LMS:Mn 4 + ) for bifunctional application in both thermometry and manometry. Upon excitation with 341 nm, LMS:Mn 4 + (0.7 % Mn 4 + ) emits a bright narrow-band red light peaking at 705 nm with an FWHM (full width at half maximum) of 32 nm. As a thermometer, when the temperature surpasses 298 K, non-radiative transitions from the 2 E g excited state lead to a sharp decrease in decay lifetimes with increasing temperature. This allows for lifetimebased luminescence thermometry with a relative sensitivity of 2.52 % K -1 at 391 K. Moreover, LMS:Mn 4 + was processed into a temperature-sensing coating and its non-contact thermometry functionality was validated. In manometry applications, the LMS:Mn 4 + probe experiences substantial pressure-dependent redshift with a sensitivity of 1.20 nm GPa -1 in the testing range of 9.48 GPa, which is about 3.3 times that of conventional ruby probes. Furthermore, its FWHM consistently remains below 37 nm, which contributes to a high reliability of pressure measurements. The above results indicate that the LMS:Mn 4 + constitutes a promising bifunctional luminescence probe material in thermometry and manometry. (c) 2024 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.