Abstract:The microstructure and properties of powder metallurgy high-speed steel prepared by hot isostatic pressing with different heat treatments have been studied. The microstructure, phase composition, effect of quenching and tempering parameters, fracture morphology, and mechanical properties of the sample are discussed in detail. The H-HSS sample presents the characteristics of the powder prior to the particle boundary and consists of carbide and ferrite, in which the carbides are fine and evenly dispersed without segregation. The bending strength and hardness of the H-HSS sample are 3112 MPa and 56.3 HRC, respectively. The Q-HSS sample is mainly composed of martensite, residual austenite, and carbides. With the increase in quenching temperature, the grain size of the matrix gradually grows, and the small carbide particles dissolve into the matrix, causing an increase in carbide size and a decrease in quantity. The bending strength and hardness of the Q-HSS sample quenched at 1210 °C achieve the maximum values of 3114 MPa and 68.8 HRC, respectively. After tempering, the martensite is transformed from a quenched lath shape to a needle shape, the residual austenite content decreases, and secondary carbides precipitate from the matrix, resulting in a secondary hardening. The T-HSS sample that is quenched at 1120 °C followed by tempering at 550 °C for 20 min has the best bending strength of 4355 MPa. However, the T-HSS sample that is quenched at 1240 °C followed by tempering at 550 °C for 120 min has a maximum hardness value of 69.5 HRC. The fracture mode of Q-HSS sample is brittle fracture, and the fracture mechanism is cleavage fracture. After tempering, the fracture mechanism of the T-HSS sample presents a transitional fracture mode between the cleavage fracture and micropore aggregation fracture.

Effect of quenching temperature on microstructure,mechanical properties and wear resistance of high speed steel

Development of Powder Metallurgy High Speed Steel

Effect of Heat Treatment on Microstructure and Properties of Powder Metallurgy High-Speed Steel Prepared by Hot Isostatic Pressing

Effect of Rapid Heating and Quenching on Microstructure and Mechanical Properties of High Strength Low Alloy Steel

Study on the effect of tempering on the impact abrasive wear performance of 45Si2MnCr2Mo ultra-high strength steel

Effect of Chromium on Microstructure and Oxidation Wear Behavior of High-Boron High-Speed Steel at Elevated Temperatures

Study of the Effects on the Strengthening Mechanism and Wear Behavior of Wear-Resistant Steel of Temperature Controlling in Heat Treatment

Influence of Tempering Time on the Microstructure and Mechanical Properties of AISI M42 High-Speed Steel

Effect of machining processes on the quenching and tempering surface layer of ultra-high strength steel

Microstructural evolution and tribological properties of M2 high-speed steel fabricated under various selective electron beam melting processing parameters

Effect of Quenching and Tempering Treatment on Microstructure and Mechanical Properties of CSS-42L Bearing Steel

Effect of quenching temperature on microstructure and properties of low silicon hypereutectic high chromium cast iron

Mechanical and tribological assessments of high-vanadium high-speed steel by the conventional powder metallurgy process

Effect of Deep Cryogenic Time on Martensite Multi-Level Microstructures and Mechanical Properties in AISI M35 High-Speed Steel

Effect of Spheroidizing Annealing Process on Microstructure and Properties of Quenching and Tempering 60Cr16MoMA Martensitic Stainless Steel

Effect of Tempering Conditions on Secondary Hardening of Carbides and Retained Austenite in Spray-Formed M42 High-Speed Steel

Microstructural Evolution, Behavior of Precipitates, and Mechanical Properties of Powder Metallurgical High-Speed Steel S390 During Tempering

The Effect of Long-Time Austenization on the Wear Resistance and Thermal Fatigue Properties of a High-Speed Steel Roll

Effect of quenching temperature on microstructure and properties of multivariate high chromium cast iron

Effect of Heat Treatment on Microstructure and Properties of Improved 40crni2si2mov Steel

Microstructural variations and mechanical properties of deep cryogenic treated AISI M35 high-speed steel tempered at various temperatures