Abstract:The microstructure and properties of powder metallurgy high-speed steel prepared by hot isostatic pressing with different heat treatments have been studied. The microstructure, phase composition, effect of quenching and tempering parameters, fracture morphology, and mechanical properties of the sample are discussed in detail. The H-HSS sample presents the characteristics of the powder prior to the particle boundary and consists of carbide and ferrite, in which the carbides are fine and evenly dispersed without segregation. The bending strength and hardness of the H-HSS sample are 3112 MPa and 56.3 HRC, respectively. The Q-HSS sample is mainly composed of martensite, residual austenite, and carbides. With the increase in quenching temperature, the grain size of the matrix gradually grows, and the small carbide particles dissolve into the matrix, causing an increase in carbide size and a decrease in quantity. The bending strength and hardness of the Q-HSS sample quenched at 1210 °C achieve the maximum values of 3114 MPa and 68.8 HRC, respectively. After tempering, the martensite is transformed from a quenched lath shape to a needle shape, the residual austenite content decreases, and secondary carbides precipitate from the matrix, resulting in a secondary hardening. The T-HSS sample that is quenched at 1120 °C followed by tempering at 550 °C for 20 min has the best bending strength of 4355 MPa. However, the T-HSS sample that is quenched at 1240 °C followed by tempering at 550 °C for 120 min has a maximum hardness value of 69.5 HRC. The fracture mode of Q-HSS sample is brittle fracture, and the fracture mechanism is cleavage fracture. After tempering, the fracture mechanism of the T-HSS sample presents a transitional fracture mode between the cleavage fracture and micropore aggregation fracture.

Microstructural Evolution, Behavior of Precipitates, and Mechanical Properties of Powder Metallurgical High-Speed Steel S390 During Tempering

Development of Powder Metallurgy High Speed Steel

Influence of Tempering Time on the Microstructure and Mechanical Properties of AISI M42 High-Speed Steel

Effect of Heat Treatment on Microstructure and Properties of Powder Metallurgy High-Speed Steel Prepared by Hot Isostatic Pressing

Microstructure Evolution and Precipitation Strengthening Behaviour of Additively Manufactured High-speed Steels

Effect of Tempering Conditions on Secondary Hardening of Carbides and Retained Austenite in Spray-Formed M42 High-Speed Steel

Microstructure Evolution and Mechanical Properties during Long-term Tempering of a Low Carbon Martensitic Stainless Bearing Steel

Microstructural variations and mechanical properties of deep cryogenic treated AISI M35 high-speed steel tempered at various temperatures

Evolution of Microstructures and Mechanical Properties with Tempering Temperature in a Novel Synergistic Precipitation Strengthening Ultra-High Strength Steel

Study on Diversified Carbide Precipitation in High‐Strength Low‐Alloy Steel during Tempering

Effect of Spheroidizing Annealing Process on Microstructure and Properties of Quenching and Tempering 60Cr16MoMA Martensitic Stainless Steel

Tempering behavior and mechanical properties of tempered AISI H13 steel

Synergetic Effects of Ferrite Content and Tempering Temperature on Mechanical Properties of a 960 MPa Grade HSLA Steel

Effect of Deep Cryogenic Time on Martensite Multi-Level Microstructures and Mechanical Properties in AISI M35 High-Speed Steel

Tailoring the tempered microstructure of a novel martensitic heat resistant steel G115 through prior cold deformation and its effect on mechanical properties

The Evolution of a Microstructure during Tempering and Its Influence on the Mechanical Properties of AerMet 100 Steel

Tempering influence on microstructural evolution and mechanical properties in a core of CSS-42L bearing steel

Effect of Temperature on Microstructure and Mechanical Properties of Fe-9Ni-2Cu Steel during the Tempering Process

Microstructure Transformation on Pre-Quenched and Ultrafast-Tempered High-Strength Multiphase Steels

Microstructure and Tempering Softening Mechanism of Modified H13 Steel with the Addition of Tungsten, Molybdenum, and Lowering of Chromium

Effect of precipitation-induced element partitioning during tempering on mechanical properties of hot-rolled 3Mn steel after intercritical annealing