Abstract:Growth of lithium (Li) filaments within solid electrolytes, leading to the mechanical degradation of electrolyte and even short circuit of cell under high current density, is a great barrier to commercial adoption of solid‐state Li metal batteries. Understanding of this electro‐chemo‐mechanical phenomena is usually hindered by the challenge of tracking local fields such as stress, displacement, and electric fields inside solid electrolyte by experimental techniques. Here, we report a multiphysics simulation aiming to investigate the evolution of mechanical failure of solid electrolyte induced by the electrochemical plating of Li inside. Visualization of local stress, resulted damage and crack propagation within solid electrolyte enables comprehensive examination of critical factors dominating the degradation process, including the geometry, number, and size of Li filaments as well as pre‐existing voids in the electrolyte. The relative damage induced by locally high stress is found to preferentially occur at the region with great fluctuation at the solid electrolyte/Li filament interface. Under the condition of multiple Li filaments in the solid electrolyte pellet, high number density of Li filament or voids triggers the integration of damage and crack networks by the enhanced propagation between adjacent filaments. Our model is built on the synchronous coupling of the mechanical behavior of solid electrolyte and the electrochemical plating of Li inside, revealing the evolution of multi‐physical fields that can barely be captured by the state‐of‐the‐art experimental techniques. The understanding for the mechanical degradation of solid electrolyte with presence of Li filaments paves the way to design advanced solid electrolyte for future solid‐state Li metal batteries. This article is protected by copyright. All rights reserved

Electrochemical Shock and Transverse Cracking in Solid Electrolytes

Transverse and Longitudinal Degradations in Ceramic Solid Electrolytes

Modeling storage particle delamination and electrolyte cracking in cathodes of solid state batteries

Unravelling the Impact of Reaction Paths on Mechanical Degradation of Intercalation Cathodes for Lithium-Ion Batteries.

Accelerated Li Penetration and Crack Propagation Due to Mechanical Degradation of Sulfide‐Based Solid Electrolyte

Electro-chemo-mechanical Failure of Solid-state Electrolyte Caused from Intergranular or Transgranular Damage Propagation in Polycrystalline Aggregates

Modeling damage to the solid electrolyte matrix in composite electrodes: role of ionic conductivity

In situ Observation of Li Deposition‐Induced Cracking in Garnet Solid Electrolytes

Electro–Chemo–Mechanical Failure of Solid Electrolytes Induced by Growth of Internal Lithium Filaments

Modeling of internal mechanical failure of all-solid-state batteries during electrochemical cycling, and implications for battery design

Visualizing plating-induced cracking in lithium-anode solid-electrolyte cells

Mechanical Failure of Solid‐State Electrolyte Rooted in Synergy of Interfacial and Internal Defects

Internal failure coupled with interfacial disintegration of solid-state electrolyte induced by the electrodeposition of lithium metal under defected interface

Role of Interfacial Defects on Electro-Chemo-Mechanical Failure of Solid-State Electrolyte.

Simulations of dendrite and crack and their interactions in solid electrolyte by phase field method

Grain Size and Grain Boundary Strength: Dominative Role in Electro-Chemo-mechanical Failure of Polycrystalline Solid-State Electrolytes

Role of interfacial defect on electro‐chemo‐mechanical failure of solid‐state electrolyte

Electro‐chemo‐mechanical failure of solid electrolyte induced by growth of internal lithium filaments

Coupled crack propagation and dendrite growth in solid electrolyte of all-solid-state battery

Visualizing Chemomechanical Degradation of a Solid-State Battery Electrolyte

Atomic mechanism of lithium dendrite penetration in solid electrolytes