Abstract:<p>Lithium metal all-solid-state batteries (ASSBs) are promising candidates for future lithium batteries thanks to their high safety performance and energy density. However, Li dendrite growth and interfacial failure are the two fatal issues deteriorating the cyclability that hinders the wide commercialization of ASSBs. To further understand the underlying mechanisms, a coupled electrochemical-mechanical phase-field model for grain crack propagation and lithium dendrite growth is proposed from the energy conservation perspective in this study. We discover that longer defect with sharp edge and angle (<span class="math"><math>θ≥45°</math></span>) causes more severe crack propagation and leads to larger dendrite growth area due to the increased strain energy density. We observe that the initial defect within grain plays an irrelevant role in the dendrite growth within the grain boundary. Stacking pressure greater than 10 MPa significantly speeds up crack propagation as well as dendrite growth due to the nontrivial mechanical driving force. Mechanical stress-induced strain-energy would contribute to more than 15% of the total dendrite growth once the stacking pressure exceeds 20 MPa, while it is trivial if the stacking pressure is below 10 MPa. Large enough fracture threshold strain can prevent the crack propagation. Results provide a fundamental tool for the design and evaluation of ASSB safety and cyclability from a more comprehensive perspective and clear the barrier for the development of next-generation ASSBs.</p>

What problem does this paper attempt to address?

The paper attempts to address two critical issues in All-Solid-State Batteries (ASSBs): lithium dendrite growth and interface failure. These problems severely affect the cycling stability and commercial application of ASSBs. Specifically: 1. **Lithium Dendrite Growth**: The growth of lithium dendrites in solid electrolytes can lead to short circuits, thereby affecting the safety and lifespan of the battery. 2. **Interface Failure**: The instability of the interface between the solid electrolyte and the electrode can also lead to a decline in battery performance. To gain a deeper understanding of the mechanisms behind these issues, the authors propose a coupled electrochemical-mechanical phase-field model to study the behavior of grain crack propagation and lithium dendrite growth from the perspective of energy conservation. Through this model, the authors explore the effects of defect length, angle, shape, and stacking pressure on crack propagation and lithium dendrite growth, providing a theoretical basis for the design and evaluation of the safety and cycling stability of ASSBs.

Coupled crack propagation and dendrite growth in solid electrolyte of all-solid-state battery