Abstract:Oxidation of metals in water has been explored to generate sustainable carbon free hydrogen and power. This paper studies the thermal ignition of micro aluminum powders in high-pressure deionized (DI) water for cogeneration of hydrogen, heat, and alumina. Thermal ignition (temperature runaway) is necessary to ensure achieving high reaction temperatures, past the saturation temperature, where alumina formation is thermodynamically favorable. Aluminum powders with nominal particle diameters of 1, 10 and 45 μm with spherical morphology and 2 μm with flake morphology were mixed with DI water to form slurries with equivalence ratio of 1.3 in a 100 mL batch reactor. The reactor was pressure maintained between 500 and 2000 psig using a back-pressure regulator, and heat was injected into the slurry through an electric band heater. It was found that 1 and 2 μm powders ignite in compressed water, but only the 2 μm slurries achieved temperatures above saturation temperature at pressures above 700 psig. On the other hand, 10 and 45 μm powders require saturated steam for ignition at pressures above 1000 and 1200 psig, respectively. Hydrogen volume data indicate that larger powders at higher pressures optimize reaction yield, which is likely due to delayed ignition which preserves the active aluminum content and the particle-water reaction interfaces. Scanning electron microscopy images illustrate that the byproduct particles crack upon ignition at the saturation temperature, which increases the specific surface area by an order of magnitude relative to the aluminum powders. Pore size distribution data indicates the formation of micro, meso and macropores upon the ignition. X-ray powder diffraction data indicate that reaction temperatures above 450 °C promote the formation of alumina (Al 2 O 3 ) instead of boehmite (ALOOH).

Popcorn-like aluminum-based powders for instant low-temperature water vapor hydrogen generation

Investigation of the effect of temperature and applied electric field on the aluminum-water reaction by ReaxFF molecular dynamics

Improved Hydrogen Generation from the Hydrolysis of Aluminum Ball Milled with Hydride

Experimental study on characteristics and mechanism of hydrogen production from aluminium–water reaction for carbon-free power generation

Study on Hydrogen Generation from the Hydrolysis of a Ball Milled Aluminum/calcium Hydride Composite

Experimental Study on the Effect of Low Melting Point Metal Additives on Hydrogen Production in the Aluminum–water Reaction

Enhanced hydrogen generation from Al-water reaction mediated by metal salts

Dynamic Process of Hydrogen and Heat Generation from Reaction of Al–Li Alloy Powders and Water Vapor at Moderate Temperatures

Hydrolysis-Based Hydrogen Generation Investigation of Aluminum System Adding Low-Melting Metals

Molten Salt-Enhanced Production of Hydrogen by Using Skimmed Hot Dross from Aluminum Remelting at High Temperature

Structural evolution of aluminum hydride nanoparticles in water using ReaxFF molecular dynamics method

Cogeneration of hydrogen, alumina, and heat from aluminum-water reactions

Metal Substrate Enhanced Hydrogen Production of Aluminum Fed Liquid Phase Ga–In Alloy Inside Aqueous Solution

Dynamic hydrogen generation phenomenon of aluminum fed liquid phase Ga–In alloy inside NaOH electrolyte

Robust and Chemically Stable Superhydrophobic Aluminum-Alloy Surface with Enhanced Corrosion-Resistance Properties

Experimental Researches on Hydrogen Generation by Aluminum with Adding Lithium at High Temperature

Hydrogen Production by the Reaction of Al-based Metals with Water Vapor

Study of a Hydrogen Inhibition Method with Sodium Tungstate for Wet Aluminum Dust Removal Systems

Hydrogen Production from Aluminum-Water Reactions at Low Temperatures: Based on an In-Situ Two Powders of Different Particle Sizes

Silver-Assisted Hydrogen Evolution from Aluminum Oxidation in Saline Media