Abstract:The Ni-Al intermetallic sheets were prepared by the reaction synthesis of pure Ni and Al foils with different thickness ratios. The first stage was performed at 640 °C/20 MPa/6 h to consume Al layers, and the second stage was performed at 1200 °C/20 MPa/1 h to complete the synthesis of Ni-Al intermetallic sheets. The thickness ratios of original Ni and Al foils strongly affected the microstructure and mechanical properties of Ni-Al intermetallic sheets. When Ni/Al thickness ratio was 1:1.5 (R1:1.5), the microstructure was single-phase NiAl with bimodal grain structure, and it transformed into coarse grains dominated single-phase NiAl structure when Ni/Al thickness ratio was 1:1 (R1:1). The microstructures changed to NiAl+Ni3Al+Ni when the ratios were 1:0.63 (R1:0.63) and 1:0.25 (R1:0.25). At ambient temperature, Samples R1:0.25 and R1:0.63 had high strength, while Samples R1:1 and R1:1.5 showed serious brittleness. At high temperature, Sample R1:1 showed preferable ductility with the elongation of 61.3%, 71.4% and 101.3% at 800 °C, 900 °C and 1000 °C, respectively; Sample R1:0.63 showed the highest tensile strength, with the values of 350.3 MPa, 230.5 MPa and 140.2 MPa at 800 °C, 900 °C and 1000 °C, respectively. For the fracture at ambient temperature, Sample R1:0.25 showed a mixed fracture mode of dimple fracture and quasi-cleavage fracture; the fracture mode of Sample R1:0.63 was mainly cleavage fracture; Sample R1:1 showed a typical brittle cleavage fracture with a large number of river-like patterns; the fracture mode of Sample R1:1.5 was brittle transgranular fracture for coarse grain layers (CGLs) and intergranular fracture for fine grain layers (FGLs). At high temperature, Samples R1:1.5 and R1:1 were mixed fracture modes of dimple fracture and quasi-cleavage fracture; the fracture mode of Sample R1:0.63 was mixed quasi-cleavage and cleavage fracture; the fracture mode of Sample R1:0.25 was single cleavage fracture with microcracks at the NiAl layers.

Effect of Electric Field on the Microstructure and Properties of NiAl Alloy Sheet Prepared by Foil Reaction Synthesis

Fabrication and mechanical properties of the NiAl sheet with a 3-dimensional network structure prepared by Ni nets and Al foils

Microstructure and high-temperature properties of NiAlV sheet prepared by magnetron-sputtering and foil-reaction

Effect of Alloying Elements and Processing Parameters on Microstructure and Properties of 1XXX Aluminium Alloys

Preparation of Nb 3 Al Superconductor by Powder Metallurgy and Effect of Mechanical Alloying on the Phase Formation

Investigating the Influence of Al Contents on Microstructure and Mechanical Properties of Ni 3 Al Superalloy Fabricated by Twin Wire‐Based Direct Arc Energy Deposition

Effect of Extrusion Process on Microstructure and Mechanical Properties of Ni3Al-B-Cr Alloy During Self-Propagation High-Temperature Synthesis

The microstructure and mechanical properties of reaction synthesized Ni-Al intermetallic sheets by pure Ni/Al foils with different thickness ratios

The Al/Ni Interfacial Reactions under the Influence of Electric Current

Microstructures and properties of in situ synthesis Ni/Ni-Al multilayer composites

Effect of Fe Addition on Microstructure and Properties of Al-3ni Alloys

Microstructural evolution and mechanical properties of Ni/Al reactive nanolaminates with different NixAly intermetallic phases

Enhanced Sintering Kinetics in Aluminum Alloy Powder Consolidated Using Dc Electric Fields

Microstructure and Mechanical Properties of Ni3Al and Ni3Al–1B Alloys Fabricated by SHS/HE

Effect of Ni addition on the microstructure, conductivities and mechanical properties of as-cast Al-Fe alloys

Fabrication of NiAl alloy hollow thin-walled component through hot gas forming of Ni/Al laminated tube and conversion process

Microstructure and formation mechanism of Ni-Al intermetallic compounds fabricated by reaction synthesis

Effects of Ni Foil Thickness on the Microstructure and Tensile Properties of Reaction Synthesized Multilayer Composites

Reaction Synthesis of Nickel/Aluminide Multilayer Composites Using Ni and Al Foils: Microstructures, Tensile Properties, and Deformation Behavior

Effect of microalloying additions on microstructural evolution and thermal stability in cast Al-Ni alloys

Microstructure Evolution and Mechanical Properties of Ni3al/Al2o3 Composite During Self-Propagation High-Temperature Synthesis and Hot Extrusion