Synthesis and Properties of Linseed Oil-Based Waterborne Non-Isocyanate Polyurethane Coating

Zichen Ling,Qixin Zhou

DOI: https://doi.org/10.1039/d3gc03249c

IF: 9.8

2023-01-01

Green Chemistry

Abstract:Linseed oil-based cyclic carbonate was synthesized via thiol–ene reaction and esterification. This cyclic carbonate was subsequently utilized for the synthesis of waterborne non-isocyanate polyurethane.

What problem does this paper attempt to address?

Synthesis of CO2-Derived, Siloxane-Functionalized Poly(ether Carbonate)s and Waterborne Polyurethanes

Zhongzhu Ma,Xianwei Zhang,Xiaojing Zhang,Numan Ahmed,Hong Fan,Jintao Wan,Carla Bittencourt,Bo-geng Li

DOI: https://doi.org/10.1021/acs.iecr.9b06795

2020-01-01

Industrial & Engineering Chemistry Research

Abstract:Siloxane-functionalized poly(ether carbonate)s (Si-PECs) were synthesized from terpolymerization of carbon dioxide (CO2), propylene oxide (PO), and [3-(2,3-epoxypropoxy)propyl]-trimethoxysilane (KH-560). Si-PECs with different molecular weights (1500-4000 Da) and siloxane content (0-9.8% by mole) were obtained and used as the soft segments of waterborne polyurethane (WPU). The carbonate unit in polyols improved the mechanical and oxidation resistance of WPU, whereas the siloxane units offered higher cross-linking density and thermal stability. The particle size of the Si-PEC-WPU emulsion varied from 100 to 684 nm as the siloxane unit content in Si-PEC increased. Further, the Si-PEC-WPU film prepared from Si-PEC having an M-n of 2200 and a siloxane content of 3.9% by mole showed not only excellent mechanical performance with a tensile strength of 16.5 MPa and elongation at a break of 683.4% but also good hydrophobicity because of the carbonate units and siloxane units. To summarize, Si-PECs derived from CO2 and inexpensive silane coupling agents show good promise as an alternative for commodity polyols for WPU applications.
Properties of Waterborne Polyurethane Latex for Environmental Friendly Leather Finishing Agent

Fu-quan CAI,Ling-shu WAN

DOI: https://doi.org/10.3969/j.issn.1674-0939.2011.04.003

2011-01-01

Abstract:Environmental friendly leather finishing agent based on polyurethane has attracted great attention in recent years.In this paper we reported the synthesis of polyurethane latex through pre-polymerization,chain extension,neutralization and emulsification using organic siloxane polymer as the modifier.The surface composition,surface hydrophilicity,and mechanical properties were investigated.The results indicated that the resultant latex could be stored up to one year.Furthermore,due to the introduction of organic siloxane blocks and the in situ crosslinking during the film formation,the coating was hydrophobic and showed excellent crocking fastness.
Synthesis of Linseed Oil-Based Waterborne Urethane Oil Wood Coatings

Chia-Wei Chang,Jing-Ping Chang,Kun-Tsung Lu

DOI: https://doi.org/10.3390/polym10111235

IF: 5

2018-11-07

Polymers

Abstract:The linseed oil glyceride (LOG) was synthesized by using a transesterification process with a glycerol/linseed oil molar ratio of 1.0. The waterborne urethane oil (WUO) wood coating was prepared by acetone process. First, dimethylolpropionic acid was reacted with hexamethylene diisocyanate (HDI) or isophorone diisocyanate (IPDI), followed by adding LOG at various NCO/OH molars of 0.7, 0.8, and 0.9, respectively, and the COOH-containing prepolymer was obtained. Then, the ionomer which was prepared by neutralizing prepolymer with trimethylamine, was dispersed by adding deionized water, and the water–acetone dispersion was obtained. Finally, the acetone was removed by vacuum distillation. In the whole synthesized process, the LOG and COOH-containing prepolymer could be steadily synthesized by FTIR analysis, and the weight-average molecular weight and polydispersity of COOH-containing prepolymer increased with an increase of NCO/OH molar ratios. During the water dispersion process of the ionomer acetone solution, the point of phase inversion was prolonged, meaning the solid content decreased with an increase of NCO/OH molar ratios. After acetone was removed, the color of WUO was milky-white, and it was weakly alkaline and possessed a pseudoplastic fluid behavior. The particle size of WUO increased with increasing of NCO/OH molar ratios, however, the storage stability was extended for HDI and shortened for IPDI synthesized with increasing of NCO/OH molar ratios.

polymer science
Synthesis and Characterization of Eugenol‐based Silicone Modified Waterborne Polyurethane with Excellent Properties

Xiaojing Zhang,Yuquan Cai,Xianwei Zhang,Tariq Aziz,Hong Fan,Carla Bittencourt

DOI: https://doi.org/10.1002/app.50515

IF: 3

2021-01-01

Journal of Applied Polymer Science

Abstract:A eugenol-based silicone-containing monomer 4,4 '-(1,1,3,3-tetramethyldisiloxane-1,3-dipropyl)bis-2-methoxyphenol(EUSi) was synthesized from eugenol and 1,1,3,3-tetramethyldisiloxane via the hydrosilylation reaction. And waterborne polyurethane (WPU) with excellent properties was obtained by using EUSi as a type of diol chain extender. The unique combination of rigidity and flexibility in the chemical structure of EUSi greatly facilitated the mechanical properties, thermal properties, and water resistance of WPU. With only a 3% dosage of EUSi, the maximum tensile strength was increased from 6.2 to 22.4 MPa, while the water absorption was decreased from 31.3% to a surprisingly 7.6%. Our work provides a new convenient strategy for the preparation of organosilicon-modified WPU with improved performance.
Synthesis of Waterborne Polyurethane and Properties of Solidified Coating

Lijun LIU,Keda WANG,Xin JIN,Yingyan JIANG,Liming TANG

DOI: https://doi.org/10.3969/j.issn.1001-702x.2009.01.013

2009-01-01

Abstract:A waterborne polyurethane emulsion with carboxyl groups was synthesized taking toluene diisocyanate (TDI),2,2-dimethylolpropionic acid(DMPA),polyethylene glyco(lPEG) and glycolic acid(GA)as main raw material. With 1-aziridinyl ethanol as the cross linker and cured at room temperature,the obtained coating material possessed excellent water resistance and mechanical properties.
Synthesis and properties of castor oil–based cationic waterborne polyurethane modified by epoxy resin

Xiufen Liu,Fengyuan Sun,Yifan Liu,Baojian Yao,Haishan Liang,Minghao Mu,Xinqiang Liu,Haisong Bi,Zheng Wang,Chengduo Qian,Xue Li

DOI: https://doi.org/10.1007/s00396-023-05174-2

IF: 2.4

2023-10-01

Colloid & Polymer Science

Abstract:Waterborne polyurethane (WPU) has gained widespread attention. However, conventional linear WPU emulsions have lower mechanical properties, poor water resistance, and other disadvantages. In this study, polyurethane prepolymers containing branched chains were successfully synthesized by using diphenylmethane diisocyanate (MDI), polytetramethylene ether glycol (PTMG) and castor oil (CO) as the main raw materials. On this basis, epoxy resin was used to further modify the obtained polyurethane prepolymers, which results in an increase in mechanical properties, water resistance, and heat resistance due to the formation of a network cross-linked structure during the film formation. The type and addition amount of epoxy resin were determined by centrifugal stability and particle size of WPU emulsions, water absorption, and mechanical properties of WPU films. The results showed that the prepared epoxy resin–modified WPU (EWPU) emulsions have excellent centrifugal stability. If 7% epoxy resin was added after the polyurethane chain expansion, the corresponding EWPU films have good mechanical properties (the tensile strength of 28.7 MPa and the elongation at break of 379%), water resistance (water absorption of 4.21%), and the thermal stability due to the cross-linked structure in EWPU. This kind of EWPU emulsions may have promising applications in coating material, adhesives, and the textile industry.

polymer science,chemistry, physical
Synthesis and Characterization of 1 K Waterborne Non-Isocyanate Polyurethane Epoxy Hybrid Coating

Zichen Ling,Cheng Zhang,Qixin Zhou

DOI: https://doi.org/10.1016/j.porgcoat.2022.106915

IF: 6.6

2022-01-01

Progress in Organic Coatings

Abstract:Non-isocyanate polyurethanes (NIPU) attract more attention these days due to the increasing environmental concerns from the traditional polyurethanes that involve isocyanates in the synthesis. Herein we prepared a novel one-package (1 K) waterborne non-isocyanate polyurethane in this study. A series of 1 K waterborne epoxy hybrid coatings were synthesized from bio-based amine, cyclic carbonate, internal emulsifier, and epoxy resin. Different formulations of the 1 K waterborne NIPU epoxy hybrid coatings were designed including different ratios of soft and hard segments, different urethane contents, and different functionalities and structures of the hybridized epoxy. The chemical structure of the NIPU polymers was analyzed by Fourier transform infrared spectroscopy and nuclear magnetic resonance. The thermal stability and mechanical property of the 1 K waterborne NIPU coatings were investigated by thermogravimetric analysis and tensile tests, respectively. One glass transition temperature studied by differential scanning calorimetry was found for each coating which demonstrated that the soft segments and the hard segments were mixed well in the 1 K waterborne NIPU coating systems. The coatings with different formulations can achieve a broad range of thermal and mechanical properties. In addition, the general coating properties, such as hardness, adhesion, and chemical resistance, were evaluated to demonstrate the practical application of the 1 K waterborne NIPU in coatings.
Synthesis of Linseed Oil Alkyd Modified Acrylic Polyurethane Resin and Electron Beam Curing Coatings

居学成,翟茂林,伊敏,哈鸿飞,蒋波,周永

DOI: https://doi.org/10.3969/j.issn.0253-4312.2000.01.003

2000-01-01

Paint and Coatings Industry

Abstract:Five different structure linseed oil alkyd modified acrylic polyurethanes have been prepared. Various properties of the electron beam cured film are tested, such as adhesion, gloss, flexibility, impact strength, hardness, tensile strength and elongation percentage etc. It has shown that the reaction is mild for preparation of linseed oils alkyd modified acrylic polyurethane; change of the structure of linseed oil alkyd modified acrylic polyurethane will affect the properties of the coatings film; in different curing systems, the effect of absorbed dosage varies; in long oil (linseed oil) system, when the cobalt naphthenate level up to 0 06%, obvious changes of film pro perties will occur.
Mechanically strong non-isocyanate polyurethane thermosets from cyclic carbonate linseed oil

Tongyao Wang,Henghui Deng,Neng Li,Fei Xie,Hebo Shi,Mengting Wu,Chaoqun Zhang

DOI: https://doi.org/10.1039/d2gc02910c

IF: 9.8

2022-09-28

Green Chemistry

Abstract:Non-isocyanate polyurethanes (NIPU) from renewable resource have attracted much attention for significant benefit for sustainable development and green production. However, the low molar mass and poor mechanical properties of NIPU greatly restricted their large-scale production and practical application as the alternatives for conventional polyurethanes. In this study, a series of bio-based carbonated linseed oil (CLSO) was synthesized via carbon dioxide (CO2) coupling reaction of epoxidized linseed oil (ELSO) followed by efficiently conversion into novel renewable NIPU thermosetting networks through curing CLSO with different diamines. In the coupling reaction between ELSO and CO2 (denoted as CO2@ELSO), the reactivity of epoxy groups at different sites on ELSO was revealed by density functional theory (DFT) calculations. Furthermore, the reaction condition for CLSO and NIPU films were optimized to achieve high atom efficiency and the tailorable performance. The tensile strength of the resulting NIPU films was high up to 69.2 MPa and the elongation at break could maintain 15.4% due to their high crosslinking density and hydrogen bonding content. The novel bio-based NIPU materials developed in this work demonstrate various advantages, including excellent mechanical properties and thermal stability, which could find various applications in coatings, adhesives, elastomers and other industries.

chemistry, multidisciplinary,green & sustainable science & technology
Waterborne Isocyanate-Free Polyurethane Epoxy Hybrid Coatings Synthesized from Sustainable Fatty Acid Diamine

Cheng Zhang,Haoran Wang,Qixin Zhou

DOI: https://doi.org/10.1039/c9gc03335a

IF: 9.8

2020-01-01

Green Chemistry

Abstract:This study proposed an effective method to prepare environmental-friendly waterborne epoxy modified non-isocyanate polyurethanes.
synthesis of Vegetable Oil Based Polyester Amide Polyols and Its Application in Water-borne PU

Yu Han-bing,Wang Xin-ling

DOI: https://doi.org/10.3969/j.issn.1009-1696.2007.03.008

2007-01-01

Abstract:Polyester amide polyols were synthesized from adipic acid and RDEA which was the mixed polyol of aliphatic alcohol amide prepared with rapeseed oil and diethanolamine.A series of polyurethaneurea(PUU)dispersions and polyurethaneurea-vinyl polymer hybrid dispersions were synthesized based on polyester amide polyols,dimethylolpropionic acid,isophorone diisocyanate,styrene and butyl acrylate.
Synthesis of novel plant oil-based isocyanate-free urethane coatings and study of their anti-corrosion properties

J. Pouladi,S.M. Mirabedini,H. Eivaz Mohammadloo,N. Ghasemi Rad

DOI: https://doi.org/10.1016/j.eurpolymj.2021.110502

IF: 6

2021-06-01

European Polymer Journal

Abstract:In this study, a bio-resource resin was synthesized via epoxidation and carbonation of linseed oil (LO) in acidic conditions, and then in the presence of tetra ‐ n ‐ butyl ammonium bromide (TBAB) and under purging of CO2 gas, respectively. The synthesized resins were characterized using FTIR spectroscopy, NMR analysis, and titration method. The resins were cured with diethylenetriamine to form non-isocyanate polyhydroxy-urethane networks. Rheometry analysis and DSC were utilized for determining the proper time and temperature of the curing process. The physical and mechanical properties of the mild steel coated samples were evaluated using various techniques. Finally, the corrosion resistance of the coated samples was assessed via Electrochemical Impedance Spectroscopy (EIS) and the results were compared with commercial polyurethane-based coated samples. The characterization tests confirmed the formation of epoxy and cyclo-carbonate groups as a result of the epoxidation process and carbonation reaction of LO, respectively. The various tests showed the appreciation of the mechanical properties of the coating samples with different carbonation weight percentages. The results revealed the improvement of adhesion and hardness properties and reduction of the flexibility of the coating samples with increasing the conversion % of carbonation. As the carbonation content increases, more hydroxyl groups were formed in the final polyhydroxy-urethane structure due to the reaction of the cyclo-carbonate with the amine, resulting in increased adhesion strength and mechanical properties of the polymer. EIS study revealed increasing of the anti-corrosion properties first and then decreasing it by increasing the percentage of carbonation. The 75% carbonated sample revealed the best corrosion performance, which was comparable with PU-based coated samples.

polymer science
Synthesis of novel propylene carbonate diol(PCD)and application in CO2-based polyols waterborne polyurethane

Zonglin He,Wenqi Xian,Zhu Ding,Chaozhi Wang,Zhenhong Huang,Lina Song,Baohua Liu

DOI: https://doi.org/10.1007/s10965-022-03288-9

IF: 3.061

2022-10-04

Journal of Polymer Research

Abstract:Propylene carbonate diols (PCD) were synthesized from propylene carbonate and ethylenediamine (EDA), iso-phorone diamine (IPDA) and diethylenetriamine (DETA), respectively. The obtained PCDs were used as extenders to prepare the waterborne polyurethane (WPU). The properties of PCD based WPUs were compared to the that of WPU used butane-1,4-diol (BDO) as extender. The structures of PCDs were characterized by Fourier transform infrared (FTIR) and nuclear magnetic resonance (NMR). The yields, melting points and viscosity of PCDs were tested. The mechanical properties, water absorption, water contact angle, adhesion, pencil hardness, thermal gravimetric analysis (TGA), differential scanning calorimeter (DSC) and dynamic mechanical analysis (DMA) of WPU films were also characterized. The results showed that PCDs with urethane bond in the structure were successfully synthesized and the yields were approximately 99% after 3 h of reaction. Compared to the WPU used BDO as extender, WPU films derived from PCDs exhibited superior tensile strength, outstanding adhesion and pencil hardness, lower water contact angle and water absorption, and higher initial thermal decomposition temperature.

polymer science
Study on Castor Oil-based Cationic Waterborne Polyurethane and Its Application

Guankun Kuang,Yan Liu,Ying Qin,Yuanyuan Zhou,Binjie Xin

DOI: https://doi.org/10.1088/1742-6596/2437/1/012030

2023-02-02

Journal of Physics: Conference Series

Abstract:The raw material for polyurethane synthesis is mainly polyols, while traditional polyols come from fossil resources. With the decrease of fossil resources, the synthesis of polyurethane by vegetable oil-based polyols has gradually gained more attention. Castor oil is a kind of plant oil-based polyols, which are the most suitable plant oil polyols because of its non-toxic, biodegradable and trihydroxy structure. Polyurethane synthesized with castor oil as a polyol has many special properties, such as good antibacterial properties, anti-UV properties, good biocompatibility and biodegradable properties. This paper explores the performance and application of castor oil-based cationic waterbased polyurethane (CWPU), which is helpful to promote its performance research and wider application.
Synthesis of poly (propylene carbonate) diol-based waterborne polyurethane modified by epoxy resin with anticorrosion properties

Yiheng Xiao,Wei Ou,Zonglin He,Zhu Ding,Jiaoyan Ai,Lina Song,Baohua Liu

DOI: https://doi.org/10.1007/s11998-023-00823-1

2023-10-29

Journal of Coatings Technology Research

Abstract:A series of modified waterborne polyurethane (WPU) with various epoxy contents was synthesized from poly (propylene carbonate) diol (PPCD)-based polyurethane prepolymer and ring-opening epoxy resin (RO-EP). The particle size, storage stability, and freeze-thaw resistance of the emulsions were examined. The pencil hardness and adhesion level of the films were tested. The structure of the modified waterborne polyurethane was characterized by Fourier transform infrared spectroscopy. The thermal stability of the modified waterborne polyurethane was studied by thermogravimetric analysis. The corrosion resistance of emulsion coating was tested by the salt spray test and electrochemical impedance spectroscopy (EIS). The waterborne polyurethane emulsion modified by RO-EP had excellent storage stability. When the content of the ring-opening epoxy resin was 10 wt%, the particle size of WPU was the smallest. The corresponding coating had excellent hardness and adhesion level. The salt spray and EIS test showed that the WPU coating with 10% RO-EP had superior corrosion resistance.
Synthesis and properties of CO2 copolymer-based waterborne polyurethane with high solid content

Wenqi Xian,Jie Yuan,Zhengbin Xie,Wei Ou,Xiaoxuan Liu,Baohua Liu

DOI: https://doi.org/10.1007/s10965-021-02616-9

IF: 3.061

2021-06-16

Journal of Polymer Research

Abstract:A series of CO2 copolymer-based waterborne polyurethanes with high solid content were successfully prepared by using CO2 copolymer diol, isophorone diisocyanate, and dimethylol propionic acid as the donors of hydrophilic groups. In order to obtain of the emulsion with high solid content and good physical property, the synthesis conditions of CO2 copolymer-based waterborne polyurethane were studied. The influence of dimethylol propionic acid content and synthesis process on the physical property of the emulsion was also investigated. Results show that CO2 copolymer-based waterborne polyurethane with high solid content can be synthesized by chain expansion at relatively low temperature. The waterborne polyurethane emulsion particle size distribution was wide. As the content of hydrophilic groups in prepolymer increased, the viscosity and water absorption increased obviously, this is difficult to synthesize waterborne polyurethane with high solid content and low water absorption. Thermal gravimetric analysis shows that the higher the chain extending temperature of CO2 copolymer-based waterborne polyurethane, the higher the thermal decomposition temperature. When the CO2 molar content of CO2 copolymer diol is about 30%, the CO2 copolymer-based waterborne polyurethane has high strength and better water resistance.

polymer science
Synthesis Technology and Properties of Waterborne Polyurethane Modified by Epoxy Resin

Zhu Lilan,Lin Xufeng,Qian Jun,Han Zhewen

DOI: https://doi.org/10.3969/j.issn.0253-4312.2012.04.010

2012-01-01

Abstract:The title waterborne polyurethane emulsion modified by epoxy resin was prepared using toluene diisocyanate(TDI),polyether(GE-210),1,4-butanediol(BDO),dimethylolpropionic acid(DMPA),epoxy resin and hydroxypropyl acrylate(HPA).Effects of the molar ratio of the —NCO and the —OH group in the prepolymer(R),the content of small molecule chain extenders,hydrophilic chain extender and epoxy resin on the size,viscosity,stability of the emulsion and water-resistance of the film was studied.The experimental results showed that the water resistance of WPU was improved,when the R was 6~7,BDO addition level was about 7%~8%,DMPA 6%~7%,epoxy resin 6%~7%,as well as good appearance and stability of the emulsion,which could be used as a WPU resin for waterborne coatings with excellent performance.
Synthesis of a Novel UV Crosslinking Waterborne Siloxane–polyurethane

Zhen Ge,Chao Huang,Chang Zhou,Yunjun Luo

DOI: https://doi.org/10.1016/j.porgcoat.2015.10.011

IF: 6.6

2016-01-01

Progress in Organic Coatings

Abstract:A novel UV crosslinking waterborne siloxane-polyurethane (UV-WPU) was synthesized using isophorone diisocyanate (IPDI), glycidyl azide polymer (GAP), polytetramethylene glycol (PTMG), dihydroxybutyl terminated polydimethylsiloxane (DHPDMS), dimethylol propionic acid (DMPA) as main materials. The structure of UV-WPU was verified using Fourier transform infrared spectroscopy (FTIR). Attenuated total reflectance (ATR) was used to study the UV crosslinking reaction kinetics of UV-WPU under UV irradiation. The properties of UV-WPU coatings by UV and thermal curing was comparatively analyzed by thermal gravimetric analysis (TGA), as well as gel fraction, water resistance and water contact measurements. The gel fraction and TGA analyses also confirmed the formation of crosslinking structure in the UV-WPU structure after UV curing process. UV-WPU cured by UV showed good thermal stability, surface properties and water resistance. (C) 2015 Elsevier B.V. All rights reserved.
Synthesis of Epoxidatied Castor Oil and Its Effect on the Properties of Waterborne Polyurethane

Zhenyang Luo,Yijun Shi,Dong Zhao,Ming He

DOI: https://doi.org/10.1016/j.proeng.2011.11.006

2011-01-01

Procedia Engineering

Abstract:In this study, a new method for synthesis poxidatied castor oil (ECO) is engaged. A series of waterborne polyurethane dispersions (WPUs) were synthesized using polytetramethylene ether glycol (PTMEG), toluene diisocyanate (TDI-80), and ECO. These WPUs can be crosslinked spontaneously upon drying, without extra additives or processing steps. Moreover, the particle size, and morphology of WPUs were examined with light scattering ultrafine particle analyzer, and transmission electron microscopy. The anti-water, thermal and mechanical properties were also studied. Results reveal that the particle size of WPUs mainly depends on the concentrations of ECO. The particle size decreases when the ECO is used. Furthermore, increased amount of ECO results in an improvement of the anti-water, thermal and mechanical properties of WPU films.
Synthesis and modification of waterborne polyurethane derived from hybrid CO2-based polyols

Yueqing Chen,Zhenhong Huang,Haijian Chen,Jiaoyan Ai,Lina Song,Baohua Liu

DOI: https://doi.org/10.1007/s10965-024-04139-5

IF: 3.061

2024-10-01

Journal of Polymer Research

Abstract:Waterborne polyurethanes emulsions (WPU) based on polyethylene carbonate diol (PECD) were synthesized, characterized and modified by polypropylene carbonate diol (PPCD) and organosilicon KH-792. The mechanical, thermal and hydrolysis resistance properties of waterborne polyurethanes were comprehensively investigated. The results show that PECD based WPU has very excellent mechanical properties. The tensile strength and the elongation at break the PU was up to 73 MPa and 1040%, which was much higher than that reported for similar types of PPCD-based WPU. It was found that water absorption of PECD based WPU can be decreased dramatically, from 40.9% to 21.1%, after 50% PECD was replaced by PPCD, while tensile strength only decreased from 73.0 MPa to 63.4 MPa. The addition of KH-792 has great influence on PECD based WPU, when 1% KH-792 was added, the water absorption rate decreased from 21.1% to 11.88%, the mechanical strength remained at 63.3 MPa, the WPU film remained transparent after soaking in 80 °C hot water for 4 h.

polymer science

Synthesis and Properties of Linseed Oil-Based Waterborne Non-Isocyanate Polyurethane Coating

Synthesis of CO2-Derived, Siloxane-Functionalized Poly(ether Carbonate)s and Waterborne Polyurethanes

Properties of Waterborne Polyurethane Latex for Environmental Friendly Leather Finishing Agent

Synthesis of Linseed Oil-Based Waterborne Urethane Oil Wood Coatings

Synthesis and Characterization of Eugenol‐based Silicone Modified Waterborne Polyurethane with Excellent Properties

Synthesis of Waterborne Polyurethane and Properties of Solidified Coating

Synthesis and properties of castor oil–based cationic waterborne polyurethane modified by epoxy resin

Synthesis and Characterization of 1 K Waterborne Non-Isocyanate Polyurethane Epoxy Hybrid Coating

Synthesis of Linseed Oil Alkyd Modified Acrylic Polyurethane Resin and Electron Beam Curing Coatings

Mechanically strong non-isocyanate polyurethane thermosets from cyclic carbonate linseed oil

Waterborne Isocyanate-Free Polyurethane Epoxy Hybrid Coatings Synthesized from Sustainable Fatty Acid Diamine

synthesis of Vegetable Oil Based Polyester Amide Polyols and Its Application in Water-borne PU

Synthesis of novel plant oil-based isocyanate-free urethane coatings and study of their anti-corrosion properties

Synthesis of novel propylene carbonate diol(PCD)and application in CO2-based polyols waterborne polyurethane

Study on Castor Oil-based Cationic Waterborne Polyurethane and Its Application

Synthesis of poly (propylene carbonate) diol-based waterborne polyurethane modified by epoxy resin with anticorrosion properties

Synthesis and properties of CO2 copolymer-based waterborne polyurethane with high solid content

Synthesis Technology and Properties of Waterborne Polyurethane Modified by Epoxy Resin

Synthesis of a Novel UV Crosslinking Waterborne Siloxane–polyurethane

Synthesis of Epoxidatied Castor Oil and Its Effect on the Properties of Waterborne Polyurethane

Synthesis and modification of waterborne polyurethane derived from hybrid CO2-based polyols