Accelerating B-Site Cation Ordering-Disordering Transition and Improving Dielectric Properties of Ba(Co,Zn)1/3nb2/3o3 Complex Perovskite Microwave Ceramics by Cuo Doping

Hao Li,Fei Liu,Chang,Xinnan Lin,Shaojun Liu

DOI: https://doi.org/10.1111/jace.19873

IF: 4.186

2024-01-01

Journal of the American Ceramic Society

Abstract:The B-site cation ordering-disordering transition process of complex perovskite Ba(B ' B-1/3 ''(2/3))O-3-based microwave ceramics can be directly promoted by accelerating the mass transport process rather than depending on long-time annealing treatment. Clear evidences suggest that CuO doping is helpful in enhancing the densification process of Ba(Co0.7Zn0.3)(1/3)Nb2/3O3 (BCZN) ceramics and promoting the growth and coarsening of the ordering domain, facilitated by the formation of quasi-liquid CuO-xCu(2)O layers. The improvement of the 1:2 ordering degree is attributed to the accelerated mass transport process enabled by quasi-liquid CuO-xCu(2)O layers rather than long-time annealing treatment. Consequently, the Qxf values experience a significant increase from 21,200 to 69,300 GHz, owing to enhancements in the relative density and 1:2 ordering degree. CuO-doped BCZN ceramics achieve high 1:2 ordering degree and Qxf values at relatively low temperatures and for short periods of time, and more importantly, it circumvents conventional lengthy annealing processes (>30 h) effectively to promote its ordering transition. These findings underscore the potential of accelerating mass transport process to promote ordering-disordering phase transitions and improving dielectric properties of complex perovskite Ba(B ' B-1/3 ''(2/3))O-3-based microwave ceramics.