Co‐optimization of Microwave Dielectric Properties in Ba(Mg1/3Ta2/3)O3 Complex Perovskite Ceramics Through Ordered Domain Engineering

Zhi Hua Kang,Rui Ze Guo,Rui Da Shi,Xiao Li Zhu,Xiang Ming Chen

DOI: https://doi.org/10.1111/jace.19007

IF: 4.186

2023-01-01

Journal of the American Ceramic Society

Abstract:It is an important subject to improve the temperature coefficient of resonant frequency (tau(f)) and thermal conductivity (kappa) of microwave dielectric ceramics without reducing the Qf value. Ordered domain engineering was applied to realize the previous objectives in Ba(Mg1/3Ta2/3)O-3 ceramics. With the increasing ordering degree from 0.835 to 0.897, the optimized Qf value was obtained. Meanwhile, near zero tau(f) from 11.9 to 5.6 ppm degrees C-1 was achieved, together with increased kappa from 5.5 to 7.6 W m(-1) K-1, and enhanced dielectric strength from 801 to 921 kV cm(-1). The noticeable ordered domain structure with large ordered domains (similar to 100 nm) and low-energy domain boundaries was revealed in Ba(Mg1/3Ta2/3)O-3. The consequent weakened phonon scattering rises the thermal conductivity. The increased bond covalency and oxygen distortion in ceramics with higher ordering degree were suggested as a cause of enlarged bandgap, which enhanced the dielectric strength. The reduced tau(f) is dominated by the less "rattling" space of the cations in the ordered state by inducing more positive tau(epsilon). The reduced tau(f), optimized thermal conductivity, and Qf value in the present work indicate that the ordered domain engineering could open up a new direction for the optimization of microwave dielectric ceramics.