A Highly Immobilized Organic Anode Material for High Performance Rechargeable Lithium Batteries
Shengnan Zhang,Shan Ren,Dongmei Han,Min Xiao,Shuanjin Wang,Luyi Sun,Yuezhong Meng
DOI: https://doi.org/10.1021/acsami.0c11241
2020-07-20
Abstract:Organic conjugated carbonyl materials have attracted considerable attention in the field of high-capacity and green energy storage technologies. However, the high solubility in organic electrolyte restrains their further application. In this work, an organic terephthalate compound (Li<sub>2</sub>M) with propargyl groups is synthesized innovatively and then used to prepare a highly cross-linked anode material (X-Li<sub>2</sub>M) by simple hydrothermal treatment for rechargeable lithium batteries. The electrochemical properties are enhanced significantly by in situ constructing an interpenetrating network of X-Li<sub>2</sub>M and the conductive carbon nanotubes (CNTs). The as-synthesized X-Li<sub>2</sub> composite anode delivers a reversible capacity of ∼200 mAh g<sup>–1</sup> at 0.1 C after 200 cycles and exhibits excellent cycle stability at a high rate of 1 C with ∼150 mAh g<sup>–1</sup> retention capacity after 1000 cycles and nearly 100% average Coulombic efficiency. Additionally, the superior rate capability is obtained at the high rate of 2 and 10 C and with specific discharge capacities of 140 and 100 mAh g<sup>–1</sup>, respectively. Highly reversible redox reaction of the electrochemical active site carbonyl group (C═O) is ascertained by ex-situ infrared spectroscopy and X-ray photoelectron spectroscopy. The described approach provides a novel direction for the immobilization of organic electrode molecules and is intended to serve as a universal guide for the research and fabrication of high-performance organic batteries.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c11241?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c11241</a>.<sup>1</sup>H NMR spectra, <sup>13</sup>C NMR spectra, TGA curves, FT-IR spectra, and DSC curves of DE(BPy-bdc), H<sub>2</sub>(BPy-bdc), and Li<sub>2</sub>(BPy-bdc); XPS spectrum of Li<sub>2</sub>(BPy-bdc) (Li<sub>2</sub>M); FT-IR spectra, XRD patterns, TGA curves, SEM images, TEM images, <sup>13</sup>C CP/MAS NMR spectra, and CV curves of Li<sub>2</sub>M and X-Li<sub>2</sub>M; TGA curves of X-Li<sub>2</sub>, X-Li<sub>2</sub>M, and CNTs; SEM and TEM images of X-Li<sub>2</sub> and CNTs; cycle performance of X-Li<sub>2</sub>M (0.1 and 1 C); cycle performance of SWCNTs (0.1 C); Nyquist plots of X-Li<sub>2</sub>, X-Li<sub>2</sub>M, and Li<sub>2</sub>M; cycle and rate performance of Li<sub>2</sub>M; photographs of X-Li<sub>2</sub> and X-Li<sub>2</sub>M cells' separators after cycling at 0.1 C for 100 cycles; SEM images of X-Li<sub>2</sub>M electrodes at different states: discharge and charge; summary of polymer electrode materials for LIB reported in recent years (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c11241/suppl_file/am0c11241_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology