Abstract:The sole micropores strictly restrict the wide utilization of TS-1 zeolite in the catalytic fields, especially in the catalytic conversion of compounds with large molecular sizes. Here, we report a feasible and economical method to overcome this drawback. In this work, the hierarchical TS-1 zeolite was constructed via post-acid treatment, post-alkali etching, and a combination of post-acid treatment and alkali etching methods, after which, the corresponding NiMo-supported catalysts were prepared via the incipient wetness impregnation method. Then, the aforementioned materials were fully characterized using X-ray diffraction (XRD), N-2 adsorption-desorption, pyridine adsorbed Fourier transform infrared spectroscopy (Py - FTIR), H-2 temperature programmed reduction (H-2 - TPR), X-ray photoelectron spectroscopy (XPS), and high-resolution transition electron microscope (HR-TEM) to unravel the changes in the physicochemical properties caused by the post treatments. Finally, the hydrodesulfurization of dibenzothiophene (DBT) was used as a probe to assess the effects of the post-treatments on the catalytic performance of the hierarchical NiMo/TS-1 catalysts. The results showed that the MFI topology of TS-1 zeolite remained undamaged significantly and the serial hierarchical TS-1 zeolites exhibited higher specific surface areas and mesopore structures. Moreover, appropriate amounts of Bronsted acid sites were formed at the surface of the serial hierarchical TS-1 zeolites. The interaction between the active metals and the support materials was also modulated by the post-treatment of TS-1 zeolite, which resulted in better dispersion of Ni promoted MoS2 slabs with a higher proportion of NiMoS active phase, further leading to the enhanced catalytic activity and direct desulfurization pathway selectivity of the corresponding serial hierarchical NiMo/TS-1 catalysts. Among all the prepared catalysts, the catalytic activity was enhanced by approximately 1.2 times over catalyst NiMo/AT-TS-1 obtained by post-acid treatment compared to that over catalyst NiMo/TS-1 without treatment and on which the selectivity of the DDS pathway was 22% higher compared to that over catalyst NiMo/TS-1.

Ni<sub>2</sub>P Catalysts Supported on Titania-Modified Alumina for the Hydrodesulfurization of Dibenzothiophene

Ni 2P catalysts supported on titania-modified alumina for the hydrodesulfurization of dibenzothiophene

Preparation of Ni<sub>2</sub>P/TiO<sub>2</sub>−Al<sub>2</sub>O<sub>3</sub>and the Catalytic Performance for Hydrodesulfurization of 3-Methylthiophene

Synthesis of Novel NiMo Catalysts Supported on Highly Ordered TiO2-Al2O3 Composites and Their Superior Catalytic Performance for 4,6-Dimethyldibenzothiophene Hydrodesulfurization

Preparation of Ni2P/TiO2−Al2O3 and the Catalytic Performance for Hydrodesulfurization of 3-Methylthiophene

Hierarchical TS-1 zeolite loaded with NiMo catalysts: Preparation and performance in hydrodesulfurization

Role of the Solvent Evaporating Temperature on the NiMo/TiO2-Al2O3 Catalyst and the Hydrodesulfurization Performance for 4,6-Dimenthyldibenzothiophehe

Effect of Supports on the Supported Ni2P Catalysts Prepared by the Phosphidation Using Triphenylphosphine in Liquid Phase

Efficient Ni2P /Al2O3 hydrodesulfurization catalysts from surface hybridization of Al2O3 particles with graphite-like carbon

Preparation of Highly Dispersed Nickel Phosphide Catalyst Supported on Nano-Sized Y Zeolite and Its Hydrodesulfurization Performance

Dibenzothiophene hydrodesulfurization activity and surface sites of silica-supported MoP, Ni2P, and Ni-Mo-P catalysts

A highly loaded and dispersed Ni2P/SiO2 catalyst for the hydrotreating reactions

A New Route for Synthesizing Nickel Phosphide Catalysts with High Hydrodesulfurization Activity Based on Sodium Dihydrogenphosphite

Highly active Ni 2 P/SiO 2 catalysts phosphorized by triphenylphosphine in liquid phase for the hydrotreating reactions

Synthesis of Supported Bimetal Phosphide Catalysts Based on Red Phosphor and Hydrodesulfurization Property

Thiophene hydrodesulfurization activities and microstructure of sulfided NiW/γ-Al2O3 catalysts

Support Effects on Thiophene Hydrodesulfurization over Co-Mo-Ni/Al2O3 and Co-Mo-Ni/TiO2-Al2O3 Catalysts

Effect of Phosphine Doping and the Surface Metal State of Ni on the Catalytic Performance of Ni/Al2O3 Catalyst

Mesoporous Carbon Supported Nickel Phosphide Catalysts Prepared by Solid Phase Reaction

Catalytic Oxidative Desulfurization of Dibenzothiophene by Composites Based Ni/Al-Oxide

Performance of Ni-rich bimetallic phosphides on simultaneous quinoline hydrodenitrogenation and dibenzothiophene hydrodesulfurization