Abstract:The electrical properties of the active precursor ions play an important role in the microstructure of the hydrodesulfurization (HDS) catalyst. Herein, this study first presents a simple strategy to adjust the charge of Mo-based nanoparticles (Mo-NPs) by changing the content of the organic complexing agent dodecyltrimethylammonium bromide (DTAB) and then investigates the effects of Mo-NPs with different charges on HDS catalysts. The results show that the zeta (zeta) potential of the Mo-NPs mutates from negative to positive with the DTA+/Mo molar ratio increasing to 4/7. Compared with conventional electronegative Mo precursors, the electropositive Mo-NPs could eliminate the electrostatic difference with the promoter nickel ions (Ni2+); thus, the Mo-NPs and Ni2+ could synchronously diffuse and co-load into the electropositive pore of gamma-Al2O3 by hydrothermal deposition, resulting in a more uniform distribution of active species (standard deviation of slab length = 0.51 vs. 1.05). Meanwhile, the isolating effect of amorphous carbonaceous species from the thermal decomposition of the organic complexing agent on the active phases was directly observed, and the stabilizer role was powerfully verified. Therefore, the resultant catalyst not only realized better Ni-promoted effects (synergetic factor = 7.5 vs. 5.3) but also exhibited excellent active phase morphology with much shorter length, higher stacking number and better dispersion. Finally, compared with the catalyst prepared from the conventional precursor, i.e. Mo7O246-, the Mo-NPs-derived catalyst shows the more excellent HDS activity of dibenzothiophene (reaction rate constant kHDS = 7.51 vs. 1.06 x 10-7 mol g-1 s-1; turnover frequency TOF = 5.56 vs. 1.43 h-1) and obviously enhanced HDS ratio of heavy coking diesel (99.8% vs. 96.2%). Besides, the resulting catalyst also holds a much higher HDS ratio as compared with the industrial catalyst (99.8% vs. 97.8%), showing a great potential in industrial application. The present work sheds light on the rational design of supported nanosized catalysts and provides a deeper understanding of the complicated structure-function relations. Using electropositive Mo-based nanoparticles (Mo-NPs) as precursor could realize the resulting catalyst with more uniform, shorter, higher layered, better Ni-promoted, and stable MoS2 slabs, thus holding excellent HDS performance.

Dibenzothiophene hydrodesulfurization activity and surface sites of silica-supported MoP, Ni2P, and Ni-Mo-P catalysts

Synthesis of Novel NiMo Catalysts Supported on Highly Ordered TiO2-Al2O3 Composites and Their Superior Catalytic Performance for 4,6-Dimethyldibenzothiophene Hydrodesulfurization

Hydrodesulfurization of 4,6-dimethyldibenzothiophene over NiMo sulfide catalysts supported on meso-microporous Y zeolite with different mesopore sizes

Role of the Solvent Evaporating Temperature on the NiMo/TiO2-Al2O3 Catalyst and the Hydrodesulfurization Performance for 4,6-Dimenthyldibenzothiophehe

Synthesis of NiMo Catalysts Supported on Gallium-Containing Mesoporous Y Zeolites with Different Gallium Contents and Their High Activities in the Hydrodesulfurization of 4,6-Dimethyldibenzothiophene

4,6-Dimethyldibenzothiophene Hydrodesulfurization on Nickel-Modified USY-Supported NiMoS Catalysts: Effects of Modification Method

Hierarchical TS-1 zeolite loaded with NiMo catalysts: Preparation and performance in hydrodesulfurization

Comparative Study on Molybdenum Nitride, Phosphide and Carbide

In Situ Synthesis of Nb-modified AFI Topology Molecular Sieve and Its Modulation on the Formantion of High-Efficiency Catalyst for 4,6-Dimethyldibenzothiophene Hydrodesulfurization

Regulating the Microenvironments and the D-Band Center of Hierarchical Nimos/Ts-1 Catalyst by Zro2 to Enhance the Hydrodesulfurization Performance of Dibenzothiophene

Effects of Pyrolyzing and Phosphiding on Dibenzothiophene Hydrodesulfurization of MOF-Derived Ni2P

Synthesis of Supported Bimetal Phosphide Catalysts Based on Red Phosphor and Hydrodesulfurization Property

MAS NMR, TPR, and TEM Studies of the Interaction of NiMo with Alumina and Silica–alumina Supports

Hydrodesulfurization of Thiophene on Ni, Mo-Supported Mcm-41 Catalysts

Synthesis and Characterization of NiMoS/TiMg and NiWS/TiMg Nanocatalysts and Their Application in the Hydrodesulfurization of Dibenzothiophene

Bimodal mesoporous AlMCM-41 supported NiMo catalysts for efficient hydrodesulfurization of 4,6-dimethyldibenzothiophene

Performance of Ni-rich bimetallic phosphides on simultaneous quinoline hydrodenitrogenation and dibenzothiophene hydrodesulfurization

MOF-derived CoP/C catalyst for efficient dibenzothiophene hydrodesulfurization

Hydrodesulfurization of Dibenzothiophene over Ni-Mo-W Sulfide Catalysts Supported on Sol-Gel Al2O3-CeO2

Fabrication of Well-Structured NiMo Hydrodesulfurization Catalysts Using Electropositive Mo-based Nanoparticles

Promoting effects of SO(4)(2-)on a NiMo/gamma-Al(2)O(3)hydrodesulfurization catalyst