Effects of Pyrolyzing and Phosphiding on Dibenzothiophene Hydrodesulfurization of MOF-Derived Ni2P

Yanyan Liu,Zhiheng Wang,Xin Li,Ruiyao Gao,Jiong Sun,Jiankun Liu,Songdong Yao

DOI: https://doi.org/10.1007/s11814-024-00100-w

IF: 2.7

2024-04-26

Korean Journal of Chemical Engineering

Abstract:To investigate the potential utilization of MOF templates in hydrodesulfurization (HDS) of large sulfur-containing compounds, MOF-derived Ni 2 P was prepared and characterized by XRD, TG, SEM, TEM, XPS and Raman. The findings indicate that MOF-derived Ni 2 P catalyst exhibits significantly enhanced Hydrodesulfurization (HDS) activity compared to conventional unsupported Ni 2 P. A modified pyrolysis and phosphiding condition allowed the stacking of central Ni atoms to be aggregated loosely, and morphology of MOF-derived Ni 2 P can be controllably transmitted from polyhedral to petal-like. A lower pyrolysis temperature tends to reduce density of Ni aggregates and cluster size of Ni 2 P(111), thereby facilitating the phosphiding of Ni aggregates and enhancing the catalytic activity of MOF-derived Ni 2 P in HDS process. Increasing the duration time of pyrolysis at lower temperatures does not accelerate the aggregation of particles, but makes petals on surface of MOF-derived Ni become thinner and eventually disappear, until coral-like nanosphere aggregates with uniform size are formed. The gradually elimination of MOF framework renders nickel aggregates more susceptible to phosphiding. The collapse of pore structure of MOF template can impact HDS activity of MOF-derived Ni 2 P. Prolonging pyrolysis time causes the spacing between Ni 2 P clusters to diminish, thereby significantly decreasing reactivity of Ni 2 P-400-4-275 compared to Ni 2 P-400-2-275 in DBT–HDS.

engineering, chemical,chemistry, multidisciplinary