Study on Oxidation Method of Corn Starch and Characterization of High Efficiency Catalyst

Yan Wang

2000-01-01

Abstract:From the comparative study of three oxidizing agents, H 2O 2, KMnO 4 and NaClO, it was suggested that the best way to produce membrane for coating from corn starch is through KMnO 4 oxidation in acidic condition.

What problem does this paper attempt to address?

Preparation of Oxidized Corn Starch in Dry Method Assisted by Kneader

Ying Li,Kang Zhang,Ya-Lu Song,Fei Cheng,Mi Zhou,Yi Lin,Pu-Xin Zhu

DOI: https://doi.org/10.1166/mex.2021.1903

2021-01-01

Materials Express

Abstract:In this study, oxidized starch (OCS) with different carboxyl content was prepared by the dry method, with H2O2 as the oxidant and CuCl2 as the catalyst. The optimum conditions were obtained by an orthogonal experiment, under the carboxyl and carbonyl content of 0.6813 and 1.0416% respectively. Fourier transform infrared (FTIR) spectroscopy, X-ray diffraction and gel permeation chromatography characterized the structures of OCS, and the thermal, gelatinization, viscosity property and its viscosity stability were measured. The results demonstrated that the crystallinity decreased slightly and the A-type crystal remained unchanged after oxidation, and the molecular weight of OCS decreased greatly. The thermal decomposition temperature, apparent viscosity and setback viscosity also decreased. With the increase of carboxyl content in OCS, the cold-water solubility and paste transparency of OCS paste increased gradually, while the viscosity of OCS paste decreased, and the viscosity stability displayed a trend of first increasing and then reducing. The OCS obtained by a kneader had low solution viscosity and high viscosity stability, suitable for sizing high count warp yarns.
Preparation and Characterization of Starch Nanocrystals Combining Ball Milling with Acid Hydrolysis.

Limin Dai,Changwei Li,Jun Zhang,Fang Cheng

DOI: https://doi.org/10.1016/j.carbpol.2017.10.015

IF: 10.723

2018-01-01

Carbohydrate Polymers

Abstract:Waxy maize starch was mechanically treated with a planetary ball mill. X-ray diffraction analysis was employed to determine the optimal ball milling time. After ball milling, the pretreated starch was hydrolyzed with H2SO4. The hydrolysates were obtained and their relative crystallinity, morphology, and particle size were estimated by X-ray diffraction analysis, atomic force microscopy, and nanoparticle size analyzer, respectively. The results revealed that it is possible to obtain starch nanocrystals (SNCs) after a combination of ball milling and 3days of H2SO4 hydrolysis with a yield of 19.3wt% with a shape similar to those acquired by the conventional procedure after 5days of sulfuric acid hydrolysis, with a yield of 15.8wt%. Round-edge SNCs with an average diameter of approximately 31nm were observed. The results revealed that by controlling some parameters, certain mechanical processing methods considered unsuitable could also be applied to the preparation of SNCs.
Preparation of Oxidized Corn Starch with High Degree of Oxidation by Fenton-Like Oxidation Assisted with Ball Milling

Jiali Li,Mi Zhou,Fei Cheng,Yi Lin,Lei Shi,Pu-Xin Zhu

DOI: https://doi.org/10.1016/j.mtcomm.2019.100793

IF: 3.8

2019-01-01

Materials Today Communications

Abstract:This work aims at preparing oxidized corn starch (OCS) with high degree of oxidation using a green method. It was proposed to prepared OCS by hydrogen peroxide (H2O2) in a Fenton-like oxidation assisted with ball milling. The effects of cupric sulfate concentrations, water content, H2O2 dosage, pH and milling media on carboxyl or carbonyl content of the obtained OCS were investigated. The optimum conditions were established, under which degree of carboxyl and carbonyl substitution of OCS reached up to 0.950 and 0.573, respectively. The oxidation kinetics of starch with H2O2 was studied for a better understanding of the oxidation process. Rapid viscosity analysis (RVA), FTIR and XRD were used to characterize OCS samples. RVA demonstrated an apparent viscosity of 10 similar to 12 mPa.s for the 10 % OCS solution at 95 degrees C. FTIR revealed the formation of carbonyl group on starch molecules. XRD demonstrated the granules structure of OCS, however, with a greatly reduced crystallinity. The OCS as green materials has potential applications in textile and food industry.
Preparation and Oxidized Mechanism of Novel Water Soluble High-oxidized Corn Starch

WANG Qiu-hua,XU Xue-chun,JIANG Wen-yong,GAN Shu-cai,GUO Nan,ZOU Hai-feng

DOI: https://doi.org/10.13413/j.cnki.jdxblxb.2007.03.036

2007-01-01

Abstract:A novel method of the preparation for the high carboxyl groups and soluble oxidized corn starch was studied. The experimental conditions were optimized, the amount of sodium hydroxide, reaction temperature and time were 21 g, 100 ℃ and 3.0 h, respectively. And the carboxyl content in the oxidized corn starch reached 3.60% under the optimized conditions. The oxidized mechanism was investigated with X-ray diffraction (XRD), Scanning electron microscopy (SEM), Infrared (IR) spectroscopy and the analyses of carboxyl and carbonyl content carried out by using chemical analysis method.
Oxidation of Cornstarch Using Oxygen As Oxidant Without Catalyst

Sheng Ye,Wang Qiu-hua,Xu Xue-Chun,Jiang Wen-yong,Gan Shu-cai,Zou Hai-Feng

DOI: https://doi.org/10.1016/j.lwt.2010.05.004

2011-01-01

Abstract:In the present work, oxygen was used as an environmentally friendly oxidant without catalyst, resulting in a waste free and simple method for starch oxidation. The oxidation was performed under the conditions of oxygen in sodium hydroxide at about 100°C. It was found that the oxidation of the native cornstarch in this system depends upon the amount of sodium hydroxide, the temperature and the duration of the oxidation treatment. Twenty one gram NaOH, 100°C and 3.0h are the optimum conditions for getting the desirable water-soluble oxidized starch with carboxyl content of 3.6g/100g. The microstructure of oxidized cornstarch was characterized by scanning electron microscopy (SEM), Fourier transform-infrared (FT-IR), Carbon-13 nuclear magnetic resonance spectroscopy (13C NMR) and chemical analysis methods. The results showed that the oxidation reaction introducing carboxyl and carbonyl groups took place at OH groups of C2, C3 and C6 in the glucose units and did not cause the breakage of C–O–C linkages.
Oxidizing Effect of Corn Starch by Oxidizing with Hydrogen Peroxide Purpose Obtaining its Basis Adhesive Materials

Muzafar Samandarovich Sharipov,Dildora Murodilloyevna Tillayeva,Nodir Shavkatovich Panoyev

DOI: https://doi.org/10.4028/p-s5xyal

2024-08-26

Advanced Materials Research

Abstract:Currently, native starch as a binder and sizing component is used extremely rarely due to its inherent disadvantages. It has been replaced everywhere with modified starches of various kinds. Studies have shown that polyelectrolyte flocculants can be created on the basis of starch if ionizable groups are introduced into the macromolecules of amylose and amylopectin. At the same time, it was found that the treatment of starch with oxidizing agents (of various natures and activities) can significantly improve the functional properties of native starch when gluing, used for surface sizing, and as a binder for corrugated cardboard. In this work, we also obtained oxidized starch in order to create an adhesive binder on its basis, and only local raw materials were used. It is shown that this method makes it possible to regulate the number of functional groups (oxidizing effect, or OE) in oxidized starch and its paste viscosity within a wide range. This is achieved by changing the molar ratio of the catalyst and oxidizer. During the oxidation process, it is possible to vary the concentration ratios of the oxidizer, catalyst, and conditions. Using FeSO 4 as a catalyzer, the oxidized starch pastes show a less pronounced pseudoplasticity and are characterized by reduced viscosity. The analysis showed that during the oxidation of corn starch with hydrogen peroxide, changes in the supramolecular structure of starch are insignificant: a certain repeated decrease in the level of crystallinity takes place, which leads to a decrease in the gelatinization temperature and also the viscosity of starch pastes.
Study on Preparation and Properties of Dialdehyde Starch from Waxy Corn Starch

胡磊,高群玉

DOI: https://doi.org/10.13386/j.issn1002-0306.2012.03.067

2012-01-01

Abstract:The dialdehyde starch was prepared through oxidation reaction with waxy corn starch and sodium periodate as raw material and oxidant respectively.By the experiments of single factor,the optimal conditions of process were as follows：the ratio of sodium periodates and starch was 1.1：1,the pH of the reaction was 3.0,the temperature was 30℃,the reaction time was 2 hours,and the concentration of starch slurry was 8%,the aldehyde content of prepared sample could reach 87.36%.From the photos of polarizing microscope,the polarizing cross reduced with the increase of aldehyde content in dialdehyde starch;through the characterization of infrared spectrum,absorption peak appeared around the wave of 1729cm-1 obviously,demonstrating the existence of aldehyde content.And the Brabenderviscosity curves appeared：comparing with the native starch,the initial gelatinization points lagged behind and the peak viscosities which were lower than native starch went up with the increase of aldehyde content;X-diffraction spectrum appeared that strong peak absorption gradually disappeared with the increase of aldehyde content.
Study on Producing Porous Corn Starch

Yinghua Lu

DOI: https://doi.org/10.3875/j.issn.1006-0375.2008.06.007

2008-01-01

Abstract:This paper aims to have a discussion about the effect of the different conditions on the porosity of corn porous starch,and the possible mechanism.Optimal corn porous starch processing conditions are determined as follows: complex enzyme that could theoretically hydrolyze 30 times of 55% of the added raw starch;ratio of α-1,4-glucanglucohydrolase to α-amylase 7:1;pH 5.6;temperature 60℃;starch solid concentratio n(w/v) 60%;reation time 20h.The result shows that after the reaction the oil adsorption ratio of corn starch was increased from 16.15% to 47.59%.
Succeeded Starch Nanocrystals Preparation Combining Heat-Moisture Treatment with Acid Hydrolysis

Limin Dai,Jun Zhang,Fang Cheng

DOI: https://doi.org/10.1016/j.foodchem.2018.11.018

IF: 8.8

2019-01-01

Food Chemistry

Abstract:Heat-moisture treatment (HMT) could be applied to increase the relative crystallinity (RC) of raw waxy maize starch (WMS) and mar the dense surface of starch granules. The optimal HMT conditions including temperature, treatment time, and moisture content were determined by response surface methodology (RSM). When the temperature, treatment time, and moisture content were 99.2 degrees C, 1.8 h, and 18.2%, respectively, the maximum RC of heat-moisture treated starch (HMTS) could reach to 42.44% and more holes, depressions, and cracks appeared on the surface of HMTS. Afterwards, HMTS was subjected to acid hydrolysis to prepare starch nanocrystals (SNCs). It was confirmed that SNCs could be successfully obtained with a hydrolysis time of 4 days and a yield of 26.7%. The results revealed that this method was more effective than conventional sulfuric acid hydrolysis method with a hydrolysis time of 5 days and a yield of 15.7%.
Effect of alkali and oxidative treatments on the physicochemical, pasting, thermal and morphological properties of corn starch

Franciela Spier,Elessandra da Rosa Zavareze,Ricardo Marques e Silva,Moacir Cardoso Elias,Alvaro Renato Guerra Dias

DOI: https://doi.org/10.1002/jsfa.6049

Abstract:Background: Few studies on starch modifications using different chemical agents are available in the literature, and no reports were found on the combined effect of oxidation and alkaline treatment of corn starch. Thus this work evaluated the physicochemical, pasting, morphological, cystallinity and thermal properties of chemically modified corn starch, after either the isolated or combined action of alkaline (sodium hydroxide) and oxidative (sodium hypochlorite) treatments. Results: The highest values for the sum of carbonyl and carboxyl and enzymatic hydrolysis occurred in starches submitted to oxidative treatment at high active chlorine concentrations. The alkali treatment in isolation modified the pasting properties, reduced the paste temperature and increased the peak viscosity, breakdown, final viscosity and setback of starches. Starch modified by the action of sodium hypochlorite and hydroxide in combination presented more severe damage on granule surfaces. Conclusion: The results show that corn starch modified by the combined action of oxidative and alkaline treatments should be studied more, especially at the concentration limit of sodium hydroxide where gelatinization occurs. Under these conditions the effect of oxidation can be more intense and thus allow the production of starches with different properties and an increase in their industrial applications.
Preparation and properties of oxidized starch with high degree of oxidation

Yurong Zhang,Xiuli Wang,Guoming Zhao,Yu Wang

DOI: https://doi.org/10.1016/j.carbpol.2011.11.036

IF: 10.723

2012-01-01

Carbohydrate Polymers

Abstract:A highly efficient method for preparing oxidized starches with a high degree of oxidation (DO) was developed, using CuSO 4 and H 2O 2 respectively as a catalyst and an oxidant. The effect of different parameters including starch origin, oxidant content, temperature, catalyst content, and reaction time on the DO was investigated systematically. In the present study, only 0.5% of catalyst was added, and the reaction time could be reduced to 1 h, while in the previous study the reaction time of 72 h was necessary to achieve almost the same DO without a catalyst. The structures and properties of oxidized starches were characterized by FT-IR, DSC, TGA, XRD, and transmittance light testing. The oxidation reduced the intrinsic viscosity and thermal stability of the oxidized starches, and could change the crystalline structures into amorphous states when the DO reached 56.3%. When temperature and/or DO increased, the transmittance of suspended solution of oxidized starch increased correspondingly. © 2011 Published by Elsevier Ltd.
Starch oxidation and study of changing its properties for use as an adhesive component for the production of corrugated cardboard

Dildora Tillayeva,Muzafar Sharipov

DOI: https://doi.org/10.1051/e3sconf/202340207033

2023-01-01

E3S Web of Conferences

Abstract:It is known that for sizing papers and cardboards, starch is required, which has a lower viscosity compared to natural, increased stability and increased binding capacity. This is necessary so that the starch dispersions in the size press have a sufficiently high concentration, are process able and remain stable. The choice of an oxidizing agent and the conditions for the method of oxidizing corn starch are theoretically substantiated. The mechanism and regularities of the process of starch oxidation have been studied. Changes in the gel-forming and sorption properties of starch during its oxidation were revealed. The intervals of quantitative parameters of the components for the modification process are determined. The dependence of the surface tension of starch pastes on its concentration in solution has been obtained.
Preparation and Characterization of Modified Starch Granules with High Hydrophobicity and Flowability

Fengdan Chang,Xiaowei He,Xiong Fu,Qiang Huang,Yaofang Qiu

DOI: https://doi.org/10.1016/j.foodchem.2013.11.140

IF: 8.8

2014-01-01

Food Chemistry

Abstract:Normal cornstarch (NC) was chemically modified by octenylsuccinic anhydride (OSA) and Al2(SO4)3. The effects of the concentration of NaOH, OSA, and Al2(SO4)3 on the properties of modified starch(OS-starch-Al) were investigated. The OS-starch-Al was characterized by repose angle, activation index, inductively coupled plasma-atomic emission spectrometry (ICP-OES), light microscopy, SEM, FT-IR, and (27)Al NMR. The results showed that pH 4 was the optimum condition for Al(3+) cross-linking with OS-starch and for obtaining high flowability and hydrophobicity. When the concentration of OSA and Al2(SO4)3 was 2%, the OS-starch-Al was characterized by high flowability. A concentration of 4% OSA and Al2(SO4)3 yielded the highest activation index. The moisture content affected the flowability of native NC, but had a minor effect on OS-starch-Al. SEM and polarized microscopy revealed that the modification had slight effects on the crystalline structure and morphology of NC. During the preparation, some dust particles functioning as flow additives were produced on the surface of starch granules. The results of FT-IR, ICP-OES, and (27)Al NMR confirmed the formation of ester group and the cross-link with Al(3+).
Characterization the structural property and degradation behavior of corn starch in KOH/thiourea aqueous solution

Wenwen Li,Jinge Li,Li Cheng,Zhengbiao Gu,Chunrui Sun,Yan Hong

DOI: https://doi.org/10.1016/j.carbpol.2021.118363

IF: 10.723

2021-10-01

Carbohydrate Polymers

Abstract:Finding an efficient and eco-friendly solution for starch dissolution has attracted considerable attentions in recent years. This study investigated the structural characteristics, and degradation behavior of corn starch in KOH/thiourea aqueous solution by the comparison with DMSO/LiBr and 1-allyl-3-methylimidazolium chloride (AMIMCl). Results showed that KOH/thiourea solution was an effective solvent for corn starch dissolution (30 min with 97.01% solubility). X-ray diffraction (XRD) and 13C CP-MAS NMR spectroscopy revealed that native crystallinity of the corn starch was altered by all tested solvents, especially DMSO/LiBr and AMIMCl. Conversely, this new solvent did not change the primary molecular structure, chain-length distribution, or thermal stability of starch, compared with the native starch. Furthermore, KOH/thiourea solution was more suitable for measuring the molecular weight of corn starch, with a weight-average molecular weight (Mw) of 7.18×107 g/mol. Therefore, KOH/thiourea solution is a promising novel solvent for starch dissolution and structural exploration.

polymer science,chemistry, organic, applied
The Synthesis of Cu–Mn–Al Mixed-Oxide Combustion Catalysts by Co-Precipitation in the Presence of Starch: A Comparison of NaOH with Organic Precipitants

Bogna D. Napruszewska,Anna Walczyk,Dorota Duraczyńska,Joanna Kryściak-Czerwenka,Alicja Michalik,Robert Karcz,Michał Śliwa,Ewa M. Serwicka

DOI: https://doi.org/10.3390/catal12101159

IF: 3.9

2022-10-02

Catalysts

Abstract:Cu–Mn mixed oxides are well known as active combustion catalysts. The common method for their synthesis is based on co-precipitation, with NaOH as a precipitant, and is burdened with the possibility of introducing undesired Na contamination. This work describes the use of two organic bases, tetrabutylammonium hydroxide and choline hydroxide, as precipitating agents in a novel alkali-free route for Cu–Mn–Al catalyst synthesis. To obtain fine crystalline precursors, which are considered advantageous for the preparation of active catalysts, co-precipitation was carried out in the presence of starch gel. Reference materials prepared with NaOH in the absence of starch were also obtained. Mixed oxides were produced by calcination at 450 °C. The precursors contained MnCO3 doped with Cu and Al, and an admixture of amorphous phases. Those prepared in the presence of starch were less crystalline and retained biopolymer residues. The combustion of these residues during calcination enhanced the formation of larger amounts of the Cu1.5Mn1.5O4 spinel phase, with better crystallinity in comparison to catalysts prepared from conventionally synthesized precursors. Tests of toluene combustion demonstrated that the catalysts prepared with starch performed better than those obtained in starch-free syntheses, and that the mixed oxides obtained by the alkali-free route were more active than catalysts prepared with NaOH. Catalytic data are discussed in terms of property–performance relationships.

chemistry, physical
Effects of Oxidation and Etherification Dual-Modification on Physicochemical Properties of Corn Starch

Qun-yu GAO,Gui-fang DAI,Hang LI,Lei WU

DOI: https://doi.org/10.3969/j.issn.1000-565X.2017.09.007

2017-01-01

Abstract:By taking the corn starches of different amylose contents as raw materials and by fixing the dosage of pro -pylene oxide and sodium hypochlorite , an oxidation and etherification dual-modification was carried out so as to re-veal the effects of the modification sequence on the physicochemical properties of the corn starches .Then, the modi-fied corn starches were analyzed in terms of transparency and Brabender viscosity , and they were characterized by means of XRD.Experimental results show that (1) the carbonyl and carboxyl of the oxidized-hydroxypropylated starches have higher molar substitution degrees , while the hydroxypropyl of the hydroxypropylated-oxidized starches has a higher one; ( 2 ) the transparency of the oxidized-hydroxypropylated starches is higher than that of the hydroxypropylated-oxidized starches;( 3 ) the peak viscosity of the hydroxypropylated-oxidized starches is higher than that of the oxidized-hydroxypropylated starches;(4) both the two kinds of modification do not change the crys-tal form of starch molecules;(5) the dual-modification is closely related to the modification order , and the first re-action plays a leading role;and (6) lower amylose content is beneficial to the oxidative modification , while higher amylose content is beneficial to the hydroxypropyl modification .
Preparation and Characterization of Dialdehyde Starch by One-Step Acid Hydrolysis and Oxidation.

Yingfeng Zuo,Wenjie Liu,Junhua Xiao,Xing Zhao,Ying Zhu,Yiqiang Wu

DOI: https://doi.org/10.1016/j.ijbiomac.2017.05.188

IF: 8.2

2017-01-01

International Journal of Biological Macromolecules

Abstract:Dialdehyde starch was prepared by one-step synthesis of acid hydrolysis and oxidation, using corn starch as the raw material, sodium periodate (NaIO4) as the oxidant, and hydrochloric acid (HCl) as the acid solution. The prepared dialdehyde starch was characterized by Fourier transform infrared spectroscopy (FT-IR), X-ray photoelectron spectroscopy (XPS), and gel permeation chromatography (GPC). The results confirmed that oxidation occurred between the starch and NaIO4. The acid hydrolysis reaction reduced the molecular weight of starch and effectively improved the aldehyde group contents (92.7%). Scanning electron microscope (SEM) analysis indicated that the average particle size decreased after acid hydrolysis and oxidation reaction. X-ray diffraction (XRD) and thermal gravimetric analyzer (TGA) analysis demonstrated that the crystallinity of the obtained dialdehyde starch showed a downward trend and a decelerated thermal decomposition rate. The starch after acid hydrolysis and oxidation exhibited lower hot paste viscosity and higher reactivity.
Study on Preparation and Properties of Carboxymethyl Corn Porous Starch

Zhong XU,Ming MIAO,Peng WANG,Hai-hua ZHANG

DOI: https://doi.org/10.3321/j.issn:1002-6630.2005.10.023

2005-01-01

Abstract:In this paper, carboxymethyl corn porous starch was prepared by adding chlorine acetic acid and ethanol. The effects of the degree of substitution to temperature, time, sodium hydroxide amount, chlorine acetic acid amount and ethanol concentra- tion were also discussed. With the degree of substitution, the optimal conditions for carboxymethyl porous starch were obtained through single factor and orthogonal experiments: reaction temperature 45℃, reaction time 6h, sodium hydroxide amount 4.0g, chlorine acetic acid amount was 4.5g and ethanol concentration 95%. When compared with raw corn starch and porous starch in the physicochemical and paste rheological properties, there were more finer improvements in carboxymethyl porous starch.
Preparation of Oxidized Wheat Starch by Sodium Hypochlorite and its Properties

XU Yang,HUANG Li-xin,ZHAO Bi-qiu

DOI: https://doi.org/10.3969/j.issn.1673-9078.2010.08.009

2010-01-01

Abstract:Sodium hypochlorite was used for oxidation of wheat starch in alkaline conditions.The effects of the amount of oxidant,reaction pH,temperature and time on the carboxyl group content of the product and the properties of paste were studied.The results indicated that the carboxyl group content of the product was greatly influenced by the amount of oxidant.Little changes of the morphology and the Maltese cross of starch granules were observed during low-level hyperoxidation.The paste properties of oxidized starch were greatly changed and the carboxyl group content of the oxidized starch was the interior factors of the changes of paste properties.
Relationship Between Oxidation Degree of Starch and Its Effects on Surface Sizing

Zhang Hongwei,Tang Aimin,Chen Gang,Liu Yingyao,Tong Yafei

DOI: https://doi.org/10.3969/j.issn.1671-4571.2006.06.014

2006-01-01

Abstract:In the paper,effects of oxidized starch with different oxidation degree as surface sizing agent on properties of paper were studied by analyzing carboxyl content and surface morphology of the oxidized starch under different preparation conditions.The results showed that oxidation degree of the starch increases with the dosages of H_2O_2 and catalyst C,while decreases with the amount of water.The oxidation degree of the starch had significant effects on the properties of the paper.The oxidized starch with carboxyl contents of 0.62% and 0.72% showed the best performance.

Study on Oxidation Method of Corn Starch and Characterization of High Efficiency Catalyst

Preparation of Oxidized Corn Starch in Dry Method Assisted by Kneader

Preparation and Characterization of Starch Nanocrystals Combining Ball Milling with Acid Hydrolysis.

Preparation of Oxidized Corn Starch with High Degree of Oxidation by Fenton-Like Oxidation Assisted with Ball Milling

Preparation and Oxidized Mechanism of Novel Water Soluble High-oxidized Corn Starch

Oxidation of Cornstarch Using Oxygen As Oxidant Without Catalyst

Oxidizing Effect of Corn Starch by Oxidizing with Hydrogen Peroxide Purpose Obtaining its Basis Adhesive Materials

Study on Preparation and Properties of Dialdehyde Starch from Waxy Corn Starch

Study on Producing Porous Corn Starch

Succeeded Starch Nanocrystals Preparation Combining Heat-Moisture Treatment with Acid Hydrolysis

Effect of alkali and oxidative treatments on the physicochemical, pasting, thermal and morphological properties of corn starch

Preparation and properties of oxidized starch with high degree of oxidation

Starch oxidation and study of changing its properties for use as an adhesive component for the production of corrugated cardboard

Preparation and Characterization of Modified Starch Granules with High Hydrophobicity and Flowability

Characterization the structural property and degradation behavior of corn starch in KOH/thiourea aqueous solution

The Synthesis of Cu–Mn–Al Mixed-Oxide Combustion Catalysts by Co-Precipitation in the Presence of Starch: A Comparison of NaOH with Organic Precipitants

Effects of Oxidation and Etherification Dual-Modification on Physicochemical Properties of Corn Starch

Preparation and Characterization of Dialdehyde Starch by One-Step Acid Hydrolysis and Oxidation.

Study on Preparation and Properties of Carboxymethyl Corn Porous Starch

Preparation of Oxidized Wheat Starch by Sodium Hypochlorite and its Properties

Relationship Between Oxidation Degree of Starch and Its Effects on Surface Sizing