Abstract:The improvement of glass and glass ceramics mechanical performance, which is determined by the components and structures, has become a critical issue for various applications. In current research, alkaline earth oxides, MgO and CaO, were introduced into Li2O-Al2O3-SiO2 glass components for glass better mechanical properties. The dependency of CaO/MgO ratios on the glass structures were investigated by Raman and nuclear magnetic resonance spectroscopy. The conversion of Qn groups in glass network confirmed decreasing bridging oxygen and connectivity with the increased CaO/MgO ratios. The glass densities, molar volumes showed linear increase with the replacement small Mg2+ion with large Ca2+ ion in glass structures. The glass transition and first crystallization temperatures slightly dropped with higher CaO content, until MgO was completely replaced. The non-linear glass hardness with maximum deviation from end numbers indicated the mixed alkaline effect in Li2O-Al2O3-SiO2 glass, probably originated from the chemical bonds and topological constraints due to the coexistence of Mg and Ca in glass structure. After heat-treatment, MgAl2Si4O12 and SiO2 crystals were precipitated in Li2O-MgO-Al2O3-SiO2 glass matrix, and the crystals phases changed to the combination of MgAl2Si4O12, LiAlSi3O8, and SiO2, to LiAlSi3O8, SiO2, to LiAlSi3O8, SiO2, ZrSiO4, and finally to Li2O·Al2O3·7.5SiO2, SiO2, ZrSiO4, due to the changed ion radius and contents, with the increased CaO/(MgO+CaO) ratios. Meanwhile, the diameters of crystals grew larger. The hardness and Reduced elastic modulus of glass ceramics increased at first, from 8.30 to maximum 8.67 GPa, and from 74.00 to 84.20 GPa, with 0.2 CaO/(MgO+CaO) ratio and then dropped. The glass structures, crystals phases and sizes change were responsible for the different mechanical properties.

Effect of R_2O on the Properties of ZnO-Sb_2O_3-P_2O_5 Low-melting Glasses

The Influence of Sb<sub>2</sub>O<sub>3</sub> Addition on the Properties of Low-melting ZnO–P<sub>2</sub>O<sub>5</sub> Glasses

Effects of alkali oxides and ion-exchange on the structure of zinc-alumino-silicate glasses and glass-ceramics

FTIR and XPS studies of low-melting PbO-ZnO-P2O2 glasses

Influences of La2O3 on the Structure and Properties of 50p2o5–30sb2o3–10cao–5al2o3–5teo2 Low-Melting Glasses

Mixed Alkali-zinc Effects on Thermo-mechanical Properties in Borosilicate Glasses

Effects of K2 CO3 on the Preparation and Optical Properties of ZnO Nanocrystals Doped Zinc-Alumino-silicate Glasses

Effect of Al_2O_3 on structure and properties of Al_2O_3-K_2O-P_2O_5 glasses

La2O3 Substitution in Li-Al-P-O-N Glasses for Potential Solid Electrolytes Applications

Effects of Additives on the Thermal Properties of Low Melting Point Lead Borosilicate Glasses

Mixed Alkali Effect in Xk2o-(30−X) Na2O-30P2O5-40ZnO Glasses

Effect of ZnO content on structure and properties in high refractive index BaO-ZnO-TiO2-SiO2 glass system

Effects of Mixed Alkaline Earth Oxides Additive on Crystallization and Structural Changes in Borosilicate Glasses

Mixed CaO/MgO effect on microstructure, mechanical properties and crystallization behaviour of Li2O-Al2O3-SiO2-ZrO2-P2O5 glass

Fabrication and properties of novel low-melting glasses in the ternary system ZnO–Sb2O3–P2O5

Effect of ZrO2 on crystallization of CaO–P2O5–SiO2 glasses

PHASE TRANSITION AND PROPERTIES OF Li_2O - Al_2O_3 - SiO_2 SYSTEM GLASS- CERAMIC WITH PARTIAL REPLACEMENT OF Al_2O_3 BY ZnO

Effect of Bi2O3 content on the structure and properties of Bi2O3-B2O3-BaO-ZnO glass

Structure, Glass Stability And Rheological Properties Of Na2o-Cao-Al2o3-Sio2 Glasses Doped With Y2o3

Impact of the La2O3 Addition on the Structure, Mechanical and Radiation Attenuation Features of La2O3–ZnO–SiO2–B2O3 Glass

Effects of ZnO on Crystallization, Microstructures and Properties of BaO–Al2O3–B2O3–SiO2 Glass–ceramics