Comparative Study of Microbiologically Influenced Corrosion of Stainless Steels in Reclaimed Water in Power Plant
LI Jin,ZHANG Wanyou,LI Jiuyi,JIAO Di,CUI Lianjun
DOI: https://doi.org/10.13334/j.0258-8013.pcsee.2010.32.005
2010-01-01
Abstract:The growth characteristics of sulfate reducing bacteria(SRB),which was isolated from the slurry of cooling tower in a power plant,in real reclaimed water were studied.The process of bio-film developed on surface of SS304 and SS316L samples immersed in real reclaimed water with SRB,and the electrochemical behavior of interface between samples and bio-film were investigated using atomic force microscopy,(AFM) and electrochemical impedance spectroscopy(EIS).The results show that this strain of SRB can survive in reclaimed water.Though SS316L exhibits a more intense adsorption to SRB cell,it still has higher resistance to bio-film corrosion of SRB than SS304.After 14d immersion,the surface roughness of SS304 and SS316L was(222.948 ±16.06) nm and(249.682 ±38.18) nm,respectively.Removed the bio-film,the deepest pits of local corrosion on SS304 and SS316L surface was 541.24 nm,with a rate equivalent to 0.014 mm/a and 49.15 nm,with a rate equivalent to 0.001 mm/a,respectively.In late immersion,the polarization resistance of SS304 electrode was lower 1～2 orders of magnitude than SS316L electrode.The development process of bio-film on the surface of SS304 and SS316L samples is a dynamic equilibrium process.