Enhanced Thermoelectric Properties of p-Type Bi 0.48 Sb 1.52 Te 3 /Sb 2 Te 3 Composite
Fanfan Shi,Chang Tan,Hongxiang Wang,Xiaojian Tan,Yinong Yin,Bo Yu,Jianfeng Cai,Chenglong Xiong,Guoqiang Liu,Jun Jiang
DOI: https://doi.org/10.1021/acsami.0c15991
2020-11-10
Abstract:Constructing a nanocomposite to introduce a coherent interface is an effective way to improve the property of thermoelectric material. Here, a series composites of Bi<sub>0.48</sub>Sb<sub>1.52</sub>Te<sub>3</sub>–<i>x</i> wt % Sb<sub>2</sub>Te<sub>3</sub> (<i>x</i> = 0, 0.3, 0.5, 0.8, and 1.0) were synthesized, where the hydrothermally prepared Sb<sub>2</sub>Te<sub>3</sub> nanosheets were intimately wrapped in the solid-state-reacted Bi<sub>0.48</sub>Sb<sub>1.52</sub>Te<sub>3</sub> matrix. The formation of a coherent interface was observed and confirmed by the scanning electron microscopy characterization. As the Sb<sub>2</sub>Te<sub>3</sub> content was over 0.5 wt %, the carrier mobility could increase by 26%, while the carrier concentration decreased by 9% compared to those of the pure matrix at 300 K, enhancing the power factor to 40.1 μW/cm K<sup>2</sup>. Moreover, the Bi<sub>0.48</sub>Sb<sub>1.52</sub>Te<sub>3</sub>–0.5 wt % Sb<sub>2</sub>Te<sub>3</sub> sample exhibited a reduced lattice thermal conductivity of 0.83 W/m K at room temperature, resulting from the strengthened phonon scattering by interfaces. Combined with the manipulations of both the electronic and thermal transport by constructing a coherent interface, a maximum <i>ZT</i> of 1.05 was obtained in the <i>x</i> = 0.5 composite at 300 K, and it was improved by 20% compared with the result of the Bi<sub>0.48</sub>Sb<sub>1.52</sub>Te<sub>3</sub> matrix.This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology