Enhancing Mechanical Performance of Ti-Mo-Si Titanium Matrix Composites Via Al-doped MoSi2 Addition

Sisi Tang,Jinlong Su,Yong Han,Yaozha Lv,Yuan,Fang Li,Yaohua Zhang,Jinglian Fan
DOI: https://doi.org/10.1016/j.msea.2023.145857
IF: 6.044
2023-01-01
Materials Science and Engineering A
Abstract:Ti-Mo-Si titanium matrix composites (TMCs) with high Si content are potential for high-temperature applica-tions but show limited mechanical properties at room temperature due to the severe Ti-Si interfacial reaction. In this work, we propose a novel reinforcement alloying strategy to improve the interface bonding between matrix and reinforcement and enhance the room temperature mechanical properties of the Ti-Mo-Si TMCs. Specifically, the MoSi2 compound was mechanical alloyed with minor Al, then the effects of Al-doped MoSi2 addition on the microstructure, mechanical properties, fracture behavior and strengthening mechanisms of the Ti-Mo-Si com-posites were studied systematically. With the addition of Al-doped MoSi2, the matrix microstructure of the Ti-Mo-Si composites was refined and the mechanical properties were improved significantly. Notably, the TMC reinforced by 4 wt% Al-doped MoSi2 shows higher tensile strength and bending strength (766 MPa and 2616 MPa) than those of TMC (733 MPa and 2236 MPa) without Al-doping, respectively. The increase in strength is mainly attributed to the decrease in the volume fraction of Ti5Si3 and the tight interface bonding between the matrix and the reinforcement, leading to a high load transfer efficiency and a uniform strain distribution. In addition, dislocation strengthening and grain boundary strengthening play the key role in governing overall strength the Ti-Mo-Si composites.
What problem does this paper attempt to address?