Strengthening Mechanisms and Deformation Behavior of a Non-Equiatomic Ni35co27.5cr27.5al5ti5 High-Entropy Alloy with Spherical L12 Nanoprecipitates

Lingling Huang,Zhiqiang Fu,Chenliang Chu,Weiping Chen,Hao Wang,Daoben Zhu
DOI: https://doi.org/10.2139/ssrn.4571269
2023-01-01
Abstract:Introducing L12 precipitates into face-centered-cubic (FCC) structured equiatomic CoCrNi medium-entropy alloy (MEA) is an effective means to improve its disappointing strength (<450 MPa) at room temperature. Unfortunately, the L12 precipitates are usually obtained by complicated thermomechanical processing (TMP), accompanying the presence of cellular L12 precipitates at the grain boundaries (GBs) which are detrimental to the mechanical properties. In this work, we designed and fabricated a non-equiatomic Ni35Co27.5Cr27.5Al5Ti5 HEA consisting of sole spherical L12 nanoprecipitates without any other phases via a simplified short-term heat treatment processing, i.e., casting followed by homogenization and aging. The as-cast, homogenized and aged HEA all possess equiaxed grains, in the meantime, the as-cast HEA exhibits equiaxed dendritic microstructure. In the as-cast and aged HEA, spherical L12 nanoprecipitates are uniformly distributed in the FCC matrix, and the L12 nanoprecipitates of the aged HEA have smaller size and higher volume fraction in comparison with those of the as-cast HEA. The aged Ni35Co27.5Cr27.5Al5Ti5 HEA has the best mechanical properties among the three states, exhibiting a tensile yield strength of ~916 MPa, an ultimate tensile strength of ~1220 MPa, and a total elongation of ~21.5%. Precipitation strengthening is primarily responsible for the aged HEA. Digital image correlation (DIC) images corresponding to the tensile testing have shown that the homogenized and aged HEA exhibit uniform deformation, whereas the stress concentration could be observed in the as-cast HEA. Additionally, electron channeling contrast imaging (ECCI) analyses reveal that multiple deformation mechanisms including coherent L12 precipitates, the stacking fault (SF) network, the high-density dislocation walls (HDDWs) and dislocation cells, jointly acted as the dislocation obstacles for the aged HEA, contributing to the excellent strain-hardening ability for the outstanding strength-ductility synergy.
What problem does this paper attempt to address?