Abstract:Introducing L12 precipitates into face-centered-cubic (FCC) structured equiatomic CoCrNi medium-entropy alloy (MEA) is an effective means to improve its disappointing strength (<450 MPa) at room temperature. Unfortunately, the L12 precipitates are usually obtained by complicated thermomechanical processing (TMP), accompanying the presence of cellular L12 precipitates at the grain boundaries (GBs) which are detrimental to the mechanical properties. In this work, we designed and fabricated a non-equiatomic Ni35Co27.5Cr27.5Al5Ti5 HEA consisting of sole spherical L12 nanoprecipitates without any other phases via a simplified short-term heat treatment processing, i.e., casting followed by homogenization and aging. The as-cast, homogenized and aged HEA all possess equiaxed grains, in the meantime, the as-cast HEA exhibits equiaxed dendritic microstructure. In the as-cast and aged HEA, spherical L12 nanoprecipitates are uniformly distributed in the FCC matrix, and the L12 nanoprecipitates of the aged HEA have smaller size and higher volume fraction in comparison with those of the as-cast HEA. The aged Ni35Co27.5Cr27.5Al5Ti5 HEA has the best mechanical properties among the three states, exhibiting a tensile yield strength of ~916 MPa, an ultimate tensile strength of ~1220 MPa, and a total elongation of ~21.5%. Precipitation strengthening is primarily responsible for the aged HEA. Digital image correlation (DIC) images corresponding to the tensile testing have shown that the homogenized and aged HEA exhibit uniform deformation, whereas the stress concentration could be observed in the as-cast HEA. Additionally, electron channeling contrast imaging (ECCI) analyses reveal that multiple deformation mechanisms including coherent L12 precipitates, the stacking fault (SF) network, the high-density dislocation walls (HDDWs) and dislocation cells, jointly acted as the dislocation obstacles for the aged HEA, contributing to the excellent strain-hardening ability for the outstanding strength-ductility synergy.

Ultra‐strong high‐ductility Ni35Co35Fe10Al10Ti8B2 high‐entropy alloy strengthened with super‐high concentration L12 precipitates

Ultrastrong High-Ductility Ni<sub>35</sub>Co<sub>35</sub>Fe<sub>10</sub>Al<sub>10</sub>Ti<sub>8</su b>B<sub>2</sub> High-Entropy Alloy Strengthened with Super-High Concentration L1<sub>2</sub> Precipitates

Tailoring Phase Transformation and Precipitation Features in a Al21Co19.5Fe9.5Ni50 Eutectic High-Entropy Alloy to Achieve Different Strength-Ductility Combinations

A Precipitation-Hardened High-Entropy Alloy with Outstanding Tensile Properties

An unprecedented synergy of high-temperature tensile strength and ductility in a NiCoCrAlTi high-entropy alloy

Strengthening and Toughening of the Co34Cr32Ni27Al3.5Ti3.5 Alloy Through Coherent L12 Nanoprecipitates

A Novel L12-strengthened Single Crystal High Entropy Alloy with Excellent High-Temperature Mechanical Properties

Superior High-Temperature Properties and Deformation-Induced Planar Faults in a Novel L12-strengthened High-Entropy Alloy

Enhanced strength-ductility synergy via novel bifunctional nano-precipitates in a high-entropy alloy

A high-entropy alloy with hierarchical nanoprecipitates and ultrahigh strength

High-content ductile coherent nanoprecipitates achieve ultrastrong high-entropy alloys

L21-strengthened Body-Centered-cubic High-Entropy Alloy with Excellent Mechanical Properties

Strengthening Mechanisms and Deformation Behavior of a Non-Equiatomic Ni35co27.5cr27.5al5ti5 High-Entropy Alloy with Spherical L12 Nanoprecipitates

Enhancing Strength-Ductility Synergy in L12-strengthened High-Entropy Alloys Via Microband and Transformation Induced Plasticity

Precipitation-hardened High Entropy Alloys with Excellent Tensile Properties

Magnificent tensile strength and ductility synergy in a NiCoCrAlTi high-entropy alloy at elevated temperature

Enhanced strength in Co-free Ni47.5-xFe25Cr25AlxTi2.5 high entropy alloys via introducing dual precipitates

L21-strengthened Face-Centered Cubic High-Entropy Alloy with High Strength and Ductility

A novel L1 2 -strengthened single crystal high entropy alloy with excellent high-temperature mechanical properties

Multicomponent Ni-rich High-Entropy Alloy Toughened with Irregular-Shaped Precipitates and Serrated Grain Boundaries

Microstructure and Mechanical Behavior in a Spherical L12 Nanoprecipitates Strengthened Ni35Co27.5Cr27.5Al5Ti5 High-Entropy Alloy Fabricated by Direct Casting and Heat Treatment