Hydrogen storage in TiZrNbFeNi high entropy alloys, designed by thermodynamic calculations
Ricardo Floriano,Guilherme Zepon,Kaveh Edalati,Gabriel L.B.G. Fontana,Abbas Mohammadi,Zhongliang Ma,Hai-Wen Li,Rodrigo J. Contieri
DOI: https://doi.org/10.1016/j.ijhydene.2020.09.047
IF: 7.2
2020-11-01
International Journal of Hydrogen Energy
Abstract:<p>The hydrogen storage properties of the novel equiatomic TiZrNbFeNi and non-equiatomic Ti<sub>20</sub>Zr<sub>20</sub>Nb<sub>5</sub>Fe<sub>40</sub>Ni<sub>15</sub> high entropy alloys (HEAs) were studied. These alloys were designed with the aid of thermodynamic calculations using the CALPHAD method due to their tendency to form single C14 Laves phase, a phase desirable for room-temperature hydrogen storage. The alloys, which were synthesized by arc melting, showed a dominant presence of C14 Laves phases with the (Zr, Ti)<sub>1</sub>(Fe, Ni, Nb, Ti)<sub>2</sub> constitution and small amounts of cubic phases (<1.4 wt%), in good agreement with the thermodynamic predictions. Hydrogen storage properties, examined at room temperature without any activation procedure, revealed that a maximum hydrogen storage capacity was reached for the equiatomic alloy in comparison to the non-equiatomic alloy (1.64 wt% vs 1.38 wt%) in the first cycle; however, the non-equiatomic alloy presented superior reversibility of 1.14 wt% of hydrogen. Such differences on reversibility and capacity among the two alloys were discussed based on the chemical fluctuations of hydride-forming and non-hydride-forming elements, the volume per unit cell of the C14 Laves phases and the distribution of valence electrons.</p>
energy & fuels,electrochemistry,chemistry, physical