High-entropy alloy TiV2ZrCrMnFeNi for hydrogen storage at room temperature with full reversibility and good activation

Shivam Dangwal,Kaveh Edalati

DOI: https://doi.org/10.1016/j.scriptamat.2023.115774

2024-02-19

Abstract:The development of alloys that are hydrogenated and dehydrogenated quickly and actively at room temperature is a challenge for the safe and compact storage of hydrogen. In this study, a new high-entropy alloy (HEA) with AB-type configuration (A: hydride-forming elements, B: inert-to-hydrogen elements) was designed by considering valence electron concentration, electronegativity difference and atomic-size mismatch of elements. The alloy TiV2ZrCrMnFeNi had dual C14 Laves and BCC phases, in which C14 stored hydrogen and BCC/C14 interphase boundaries contributed to activation. The alloy absorbed 1.6 wt% of hydrogen at room temperature without any activation treatment and exhibited fast kinetics and full reversibility.

Materials Science

What problem does this paper attempt to address?

This paper mainly discusses the design of a new high-entropy alloy (HEA) - TiV2ZrCrMnFeNi for hydrogen storage at room temperature, which exhibits complete reversibility and good activation performance without any activation treatment. In this study, the authors considered the valence electron concentration, electronegativity difference, and atomic size mismatch of the elements to design this AB-type configuration alloy. The TiV2ZrCrMnFeNi alloy consists of C14 Laves phase and BCC phase, where C14 phase stores hydrogen and the C14/BCC phase interface contributes to activation. The alloy can absorb 1.6 wt% hydrogen at room temperature, demonstrating fast kinetics and complete reversibility.

The objective of this paper is to develop a HEA that can absorb and desorb hydrogen at room temperature without the need for activation treatment. By adjusting the structure and composition of the alloy, especially increasing the content of the BCC stabilizer vanadium, a coexistence structure of C14 Laves phase and BCC phase is formed, which helps facilitate the rapid diffusion and activation of hydrogen. Experimental techniques including X-ray diffraction (XRD), scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS), and electron backscatter diffraction (EBSD) were conducted to determine the crystal structure, microstructure, and hydrogen storage performance of the alloy.

The results show that the TiV2ZrCrMnFeNi alloy can reversibly store and release hydrogen at room temperature without activation treatment, exhibiting high hydrogen storage capacity and fast kinetics. This finding provides new insights for the design of hydrogen storage materials at room temperature, especially without the need for additional activation steps, which may have significant implications for future clean energy storage technologies.