Abstract:The fabrication of synthetic hydrogels, which simultaneously possess excellent mechanical properties and a high equilibrium water content (EWC) and can be potentially used to mimic the cartilage, one of the load-bearing tissues with a modulus of 1 MPa, a fracture strength of tens of MPa, an elongation at break of 100%, and an EWC of 75%, remains a difficult and challenging task. In this work, multiphysical cross-linked P(AA(w)-co-AM(x))/XG(y)-GG(z)/Fe3+/B hydrogels were designed and prepared using acrylic acid (AA) and acrylamide (AM) as polymerizable monomers; xanthan gum (XG) and guar gum (GG) as macromolecular sources of hydrogel bonds; and ferric (Fe3+) and tetraborate (B4O72-) ions as sources of ionic cross-linking. Under optimized conditions, the synergistic effects of multiple ionic hydrogen bond cross-linking networks endow the obtained P(AA(w)-co-AM(x))/XG(y)-GG(z)/Fe3+/B hydrogels with MPa levels of elastic moduli (1.4-3.3 MPa) and fracture strengths (1.5-2.6 MPa) and higher elongations at break of about 138-171% simultaneously with high EWCs above 70% (72-76%), as well as excellent self-recovery ability. Cytotoxicity tests confirmed that the P(AA(w)-co-AM(x))/XG(y)-GG(z)/Fe3+/B hydrogels exhibited excellent cytocompatibility and had no effect on the cell morphology, cell cycle regulation, and apoptosis level. More importantly, after culturing in Eagle's minimum essential medium for 72 h, the P(AA(0.4)-co-AM(2.0))/XG(1.0)-GG(1.0)/Fe3+/B and P(AA(0.6)-co-AM(2.4))/XG(1.0)-GG(1.0)/Fe3+/B hydrogels could retain excellent elastic moduli and fracture strengths as well as EWCs close to those of the cartilage.

Self-healing Poly(acrylic Acid) Hydrogels Fabricated by Hydrogen Bonding and Fe3+ Ion Cross-Linking for Cartilage Tissue Engineering

Mimicking the Mechanical Properties of Cartilage Using Ionic- and Hydrogen-Bond Cross-Linked Hydrogels with a High Equilibrium Water Content above 70%

Ultrastiff, Tough, and Healable Ionic-Hydrogen Bond Cross-Linked Hydrogels and Their Uses As Building Blocks to Construct Complex Hydrogel Structures

Tough Supramolecular Hydrogels with Excellent Self-Recovery Behavior Mediated by Metal-Coordination Interaction

Autonomous self-healing of poly(acrylic acid) hydrogels induced by the migration of ferric ions

Self‐healing and conductivity of chitosan‐based hydrogels formed by the migration of ferric ions

High-strength and self-healable poly (acrylic acid) /chitosan hydrogel with organic-inorganic hydrogen bonding networks

Preparation and properties of acrylate/polyvinyl alcohol self-healing hydrogels based on hydrogen bonds and coordination bonds

Tough, highly stretchable and self-healing poly(acrylic acid) hydrogels reinforced by functionalized basalt fibers

Dipeptide Self-assembled Hydrogels with Shear-Thinning and Instantaneous Self-healing Properties Determined by Peptide Sequences

A facile strategy to construct biocompatible poly(vinyl alcohol)-based self-healing hydrogels

Dual-crosslinked hyaluronic acid hydrogel with self-healing capacity and enhanced mechanical properties

Biosynthesis of proline in Pseudomonas aeruginosa. Partial purification and characterization of gamma-glutamyl kinase.

Tough and self-healable nanocomposite hydrogels from poly(acrylic acid) and polyacrylamide grafted cellulose nanocrystal crosslinked by coordination bonds and hydrogen bonds

Poly(acrylic acid)‐chitosan @ tannic acid double‐network self‐healing hydrogel based on ionic coordination

Self-healing hyaluronic acid hydrogels based on dynamic Schiff base linkages as biomaterials

Physically Crosslinked Poly(vinyl Alcohol)-Based Hydrogels for Cartilage Tissue Engineering

Composite Hydrogels with Rapid Self-Healing, Stretchable, Moldable and Antibacterial Properties Based on PVA/ε-Poly-L-lysine/Hyaluronic Acid

Fabrication of a Double-Network Hydrogel Based on Carboxymethylated Curdlan/Polyacrylamide with Highly Mechanical Performance for Cartilage Repair

Facile synthesis of self-healing and layered sodium alginate/polyacrylamide hydrogel promoted by dynamic hydrogen bond

Synthesis and characterization of injectable self-healing hydrogels based on oxidized alginate-hybrid-hydroxyapatite nanoparticles and carboxymethyl chitosan