Abstract:In this paper, two aspects of studies are carried out: (1) synthesis of geopolymer by using slag and metakaolin; (2) immobilization behaviors of slag based geopolymer in a presence of Pb and Cu ions. As for the synthesis of slag based geopolymer, four different slag content (10%, 30%, 50%, 70%) and three types of curing regimes (standard curing, steam curing and autoclave curing) are investigated to obtain the optimum synthesis condition based on the compressive and flexural strength. The testing results showed that geopolymer mortar containing 50% slag that is synthesized at steam curing (80°C for 8h), exhibits higher mechanical strengths. The compressive and flexural strengths of slag based geopolymer mortar are 75.2MPa and 10.1MPa, respectively. Additionally, Infrared (IR), X-ray diffraction (XRD) and scanning electron microscopy (SEM) techniques are used to characterize the microstructure of the slag based geopolymer paste. IR spectra show that the absorptive band at 1086cm−1 shifts to lower wave number around 1007cm−1, and some six-coordinated Als transforms into four-coordination during the synthesis of slag based geopolymer paste. The resulting slag based geopolymeric products are X-ray amorphous materials. SEM observation shows that it is possible to have geopolymeric gel and calcium silicate hydrate (C–S–H) gel forming simultaneously within slag based geopolymer paste. As for immobilization of heavy metals, the leaching tests are employed to investigate the immobilization behaviors of the slag based geopolymer mortar synthesized under the above optimum condition. The leaching tests show that slag based geopolymer mortar can effectively immobilize Cu and Pb heavy metal ions, and the immobilization efficiency reach 98.5% greater when heavy metals are incorporated in the slag geopolymeric matrix in the range of 0.1–0.3%. The Pb exhibits better immobilization efficiency than the Cu in the case of large dosages of heavy metals.

Structural Evolution of Geopolymers Incorporated with Heavy Metals: Solidification Mechanism of Pb<SUP>2+</SUP> and Cd<SUP>2+</SUP>

Lead zinc slag-based geopolymer: Demonstration of heavy metal solidification mechanism from the new perspectives of electronegativity and ion potential

Solidification/Stabilization of Pb2+ and Cd2+ Contaminated Soil Using Fly Ash and GGBS Based Geopolymer

MgO-based Binders with Different Formulations for Solidifying Pb and Cd in MSWI Fly Ash: Solidification Effect and Related Mechanisms

Geopolymer synthesized from electrolytic manganese residue and lead-zinc smelting slag: Compressive strength and heavy metal immobilization

Immobilization of Cu 2+ , Zn 2+ , Pb 2+ , and Cd 2+ During Geopolymerization

Decalcification effect on stabilization/solidification performance of Pb-containing geopolymers

Preparation and characterization of industrial solid waste based geopolymer for immobilizing Pb and Cd in the sediment

Heavy metals immobilization of ternary geopolymer based on nickel slag, lithium slag and metakaolin

Stabilization/solidification mechanisms of tin tailings and fuming slag-based geopolymers for different heavy metals

Quantifying gel properties of industrial waste-based geopolymers and their application in Pb2+ and Cu2+ removal

Synthesis and heavy metal immobilization behaviors of slag based geopolymer.

Synthesis of Geopolymers Using Municipal Solid Waste Incineration Fly Ash and Construction and Demolition Waste: Mechanical and Thermal Activation

Remediation of Pb–Cd contaminated soil using coal bottom ash-based geopolymer and coir: Soil remodeling and mechanism

Synthesis of tailing slurry-based geopolymers for the highly efficient immobilization of heavy metals: Behavior and mechanism

Cement and zeolite stabilization/solidification of heavy metal-contaminated sediments: 841-Day leaching characteristics, mechanisms, and microstructure

Codisposal of landfill leachate concentrate and antimony mine soils using a one-part geopolymer system for cationic and anionic heavy metals immobilization

Early solidification/stabilization mechanism of heavy metals (Pb, Cr and Zn) in Shell coal gasification fly ash based geopolymer

Mechanical Properties and Leaching Characteristics of Geopolymer-Solidified/Stabilized Lead-Contaminated Soil

The Long-Term Leaching Behavior of Heavy Metals in Geopolymers and Portland Cement Bricks Containing Mswi Fly Ash: A Comparative Study

Effective Stabilization of Cadmium and Copper in Iron-Rich Laterite-Based Geopolymers and Influence on Physical Properties