Preparation and Characterstics Analysis of Nanocellulose from Bambusa Emeiensis

Fengqiang Sun

2013-01-01

Abstract:α-cellulose was extracted from Bambusa emeiensis by means of Soxhlet extraction,bleaching and alkali treatments with sodium chlorite solution and sodium hydroxide solution.Nanocellulose was then isolated from α-cellulose by(33 wt%) sulphuric acid and ultrasonic treatment.According to the analyses of scanning electron microscopy(SEM) and transmission electron microscopy(TEM),the diameters of the nanocelluloses ranged from 10 to 25nm.The analysis of Fourier transform infrared(FTIR) spectroscopy showed that the hemicelluloses and lignin were totally removed from the raw material,and that the chemical components of α-cellulose and nanocellulose were basically the same.The thermogravimetric analysis(TGA) showed higher thermal stability of α-cellulose and nanocellulose after the extraction of hemicelluloses and lignin from the samples,although the nanocellulose began to degrade at a little bit lower temperature than α-cellulose.The analysis of X-ray diffraction(XRD) showed that,at different purification stages,the crystallinity of α-cellulose and nanocellulose increased significantly,and all samples presented the typical structure of cellulose I.