High Frequency Ultrasound Preparation Of Tempo-Oxided Ultrafine Cellulose Nanofibrils Of Angstrom-Scale

Gui-Chao Ye,Yun Lu,Ya-Fang Yin,Dong-Jiang Yang,Jin Sun,Xi-Lin She,Yan-Zhi Xia

DOI: https://doi.org/10.11777/j.issn1000-3304.2017.16200

2017-01-01

Acta Polymerica Sinica

Abstract:The commercial bleached bamboo was oxidized to TEMPO-oxidized cellulose nanofibrils (TOCNs) with hundreds of nanometers in length, less than 5 nm in width and the thickness less than 1 nm, which was done through TEMPO (2,2,6,6-tetramethylpiperidine-1-oxyl radical)-mediated oxidation and successive mild disintegration in water solution combined with high frequency ultrasonic treatment. The shape and dimensions of these sheets (termed "nanoribbons" hereafter), composed of many mono-and multi-layered molecular sheets, were analyzed by scattering and spectroscopy techniques to understand the structural changes. The morphology of the raw material and two types of TOCNs nanoribbons were characterized by field emission scanning electron microscope (FESEM). And the three-dimensional morphologies of the same two TOCNs samples were measured through transmission electron microscope (TEM) and atomic force microscope (AFM). The results revealed that the TEMPO-mediated oxidization systems processed in cellulose I-beta intra-layer hydrogen bonds and the long axis direction of elementary fibrils (composed by 36 cellulose chains), which was explained based on the three dimensional size difference and the change of the crystalline structure in TOCNs nanoribbons. The structures of different nanoribbons were analyzed by Fourier infrared absorption spectrum (FTIR), X-ray diffraction (XRD) and cross polarization and magic angle spinning solid-state C-13 nuclear magnetic resonance (CP/MAS C-13-NMR). FTIR analysis indicated that structure of the cellulose nanofibrils was changed during oxidization, significant amount of C6 carboxylate groups were selectively formed on each cellulose nanofibril surface by TEMPO-mediated oxidation without any changes to the original crystalline structure. XRD analysis indicated that the cellulose elementary fibrils were broken mainly along its (101) planes in TEMPO/NaClO/NaClO2 and TEMPO/NaClO/NaBr oxidized systems under high frequency ultrosonic treatment, while the I-beta crystalline structure was retained. CP/MAS 13C-NMR results were in accordance with the analyses from XRD and Raman spectra. Moreover, the oxidization scheme was important to explain the structures of the final products. This research has important significance for design, development and application of ultrafine biomass cellulose nanoribbons.