Abstract:Propose a rolling method to efficiently prepare fiber metal laminates. The surface of Al alloy sheets is treated with laser and coupling agent to achieve the purpose of toughening interface of composite laminates. In this study, a highly efficient method for preparing Al/CFRTP/Al composite laminates by roller preparation was proposed. Three different surface treatments, namely, anodic oxidation, laser texture and surface modification, were used to improve the strength of the metal‐fiber interface. Results show that composite laminates can be prepared efficiently by using reasonable roll pressing technology. The composite laminates with a thickness of 3 mm has good shear strength when the reduction amount is 0.02 mm. Laser texturing increases the contact area at the laminate interface. The surface roughness of Al alloy sheet is improved after laser texture. Moreover, the matrix in the fiber layer of the laminate can be embedded in the gullies formed by the laser texture to form a mechanical interlocking structure. The shear strength of the laminates was further increased when the laser scanning spacing was 2 mm. The highest shear strength of the laminate is 52.4 MPa after using a coupling agent to modify the surface of the Al alloy sheet. X‐ray photoelectron spectroscopy analysis showed that a new chemical bond was generated at the interface between CFRTP and the Al alloy sheet modified with silane coupling agent, thereby forming a molecular bridge among different materials. Mechanical interlocking structure and the generation of new chemical bonds cause the interface to need to absorb more energy during the failure process, which is conducive to the improvement of the interface strength. Highlights Propose roller pressing to prepare Al/CFRTP/Al composite laminates. Effect of laser texture of the laminates interface is clarified. Mechanism of coupling agents at the interface has been elucidated. Efficient preparation of thermoplastic fiber metal laminates has been achieved.

Review of Rolling Technology on Bond Strength of Rolling-Bonded Bimetal Laminates

Research Status of Bimetal Laminated Composite Plate Prepared by Rolling Process

Recent advances and trends in roll bonding c bonding model: A review

Velocity Field Analysis of Bonding Interface on Cold-Rolled Copper/Aluminum Composite Plate

Achieving excellent strength-elongation synergy in corrugated Cu/Al laminated composites by flat finish roll bonding

Interface evolution and strengthening of two-step roll bonded cu/Al clad composites

Steel–Steel Laminates Manufactured via Accumulative Roll Bonding

Bonding mechanism and preparation process of titanium/iron composite thin sheet by non-vacuum rolling

Accumulative Roll-Bonding of Aluminum Alloys and Composites: an Overview of Properties and Performance

The Role of Interfaces on the Deformation Mechanisms in Bimodal Al Laminates Produced by Accumulative Roll Bonding

Microstructure and Mechanical Properties of AA1050/AA6061 Laminated Composites Fabricated through Three-Cycle Accumulative Roll Bonding and Subsequent Cryorolling

Rolling of aluminum/steel bimetal plate with multi-lager spray deposition

Gradient alternating deformation mechanism of two metals and interface bonding mechanism of cu/Al cold rolling composite process

Effects of asymmetry and annealing on interfacial microstructure and mechanical properties of Cu/Al laminated composite fabricated by asymmetrical roll bonding

Enhancement of Adhesion Strength by Micro-Rolling-based Surface Texturing

Effects on the Microstructure Evolution and Properties of Graphene/Copper Composite during Rolling Process

Rolling preparation process and interface toughening mechanism of Al/CFRTP/Al composite laminates

Deformation Behavior and Strengthening Mechanisms of Multilayer SUS304/Cr17 Steels with Laminate/Network Interface

Effect of cumulative deformation and interlayer mechanical properties on bonding strength of corrugated interface steel/aluminum composite plate

Bonding Property of Cu/Mo/Cu Cladding Metal Materials by Hot Rolling

Effect of intermetallic compounds (IMCs) on the interfacial bonding strength and mechanical properties of pre-rolling diffusion ARBed Al/Ti laminated composites