Abstract:Abstract Here, numerous oxygen-containing functional groups were grafted onto the surface of CNTs to improve their dispersibility in an electrolyte. The CNTs were characterized by FT-IR, Raman, XPS, FE-SEM, and TEM. The results revealed that the dispersibility of the functionalized CNTs in the composites was better than unfunctionalized CNTs. CNTs/Ni composites were deposited on a copper plate by pulsed electrodeposition and ultrasonic dispersion using an electrolytic bath with CNTs concentrations from 0 to 2 g l −1 . The friction and wear behavior of the composite coatings were assessed using two different methods. In the first method, the coatings were scratched with a progressively higher load from 0–100 N, and the results demonstrate a 10 percent reduction in the coefficient of friction (COF) of the composite compared to pure nickel. The other method involved applying a constant load of 30 N, the COF and microscopic wear mechanism were investigated at different carbon nanotube contents, and the results confirmed that the COF of the composites was gradually reduced with the increase of carbon nanotube mass concentration, and the COF was only 0.343 when the carbon nanotube content was increased to 2 g l −1 . According to the XRD results, increasing the CNTs contents changed the preferred growth orientation. Moreover, the FE-SEM images of the wear surface of the 1 g l −1 CNTs/Ni sample indicated that it had the best wear resistance and showed the smoothest wear trace without apparent cracks. The addition of CNTs enhanced the wear resistance of the nickel matrix due to the superior mechanical strength and lubricating effect of the CNTs. CNTs exposed to the matrix surface reduced the direct contact between the Ni matrix and the friction pair, acted as lubricants, and reduced the wear rate.

Electroless Plating Ni-P Matrix Composite Coating Reinforced by Carbon Nanotubes

Influence on (Ni-P) Electroless Composite Plating with Carbon Nanotubes

Preparation and Tribological Properties of the Carbon Nanotubes–ni–p Composite Coating

Corrosion Behavior and Wear Resistance Characteristics of Electroless Ni-P-CNTs Plating on Carbon Steel

SYNTHESIS AND THE PERFORMANCE OF CARBON NANOTUBES-(Ni-P) COMPOSITES

Tribological properties of Ni–P-multi-walled carbon nanotubes electroless composite coating

Tribological-behavior of electroless Ni-P-carbon nanotube comoposite coating

Electroless Preparation and Tribological Properties of Ni-P-Carbon Nanotube Composite Coatings under Lubricated Condition

Electrodeposition and Mechanical Characterization of Ni-carbon Nanotubes Composite Coatings

Tribological Application of Carbon Nanotubes in a Metal-Based Composite Coating and Composites

Effects of the CNT Content and Plating Solution Ph after Purification on the Performance of Ni–P/CNT Composite Coating

Research of Carbon Nanotubes with Electroless Plating of Cobalt

Electrodeposition and Properties of Composites Consisting of Carbon Nanotubes and Copper

Influence of Carbon Nanotube Coatings on Carbon Fiber by Ultrasonically Assisted Electrophoretic Deposition on Its Composite Interfacial Property.

Investigation of the microstructure and tribological properties of CNTs/Ni composites prepared by electrodeposition

Research of Carbon Nanotubes with Electroless Plating of Nickel

Corrosion Behavior of Carbon Nanotubes–ni Composite Coating

Preparation and Characterization of Electroless Ni-P Alloy Coating on Multi-Walled Nanotubes

Electrodeposition of Ni Matrix Carbon Nanotubes Composite Films

Influence of Plating Time and Concentration on the Thickness of the Ni Coating on Carbon Nanotubes

Friction and wear behaviors of electrodeposited Ni-P-CNTs composite coatings on Al-alloy substrate