Abstract:Aqueous polyurethane (PU) prepolymers were synthesized by emulsion polymerization in situ, with toluene diisocyanate (TD1-80), polyether binary alcohol (N210), dimethylol propionic acid (DMPA), hydroxyl ethyl methacrylate (HEMA), adipic dihydrazide (ADH) and diacetone acrylamide (DAAM) as the materials. Three kinds of aqueous polyurethane-acrylate (PUA) hybrid emulsions marked as PUA-1 (free cross-linking), PUA-2 (synthesized cross-linking) and PUA-3 (cross-linking at ambient temperature) were synthesized after the free radical polymerization by adding initiator, which were then used to prepare three kinds of varnishes. The effects of the dosages of DMPA, HEMA, ADH and DAAM on the properties of emulsions and films were finally investigated. It is found that, when the mass fraction of -COOH in DMPA and the mass fractions of HEMA, ADH and DAAM in PU are respectively 2.5%, 1.44%, 3.5% and 2.0%-3.0%, the emulsions and films are all of good properties. Moreover, the results obtained by particle size analyzer and TEM show that (1) the average particle sizes of PUA-1, PUA-2 and PUA-3 are respectively 40-50 nm, 90-100 nm and 30-40 nm; (2) PUA-1 particles are regular sphericities in shape, while PUA-2 particles are irregular sphericities with interpenetrating polymer network between the core and the shell; (3) as compared with PUA-1, PUA-2 is of larger particle size and wider particle size distribution; (4) PUA-3 is of very irregular particle shape, uniform particle size distribution and disorganized interpenetrating network between the shell and the core. Furthermore, in the three kinds of vanishes, the one prepared from PUA-3 is of the best water resistance, dry-heat resistance and stain resistance but is of the longest drying time for the film.

Synthesis and Characterization of Self-Crossllnkable Water-borne Polyurethane Dispersion

Synthesis and Characterization of Water-Borne Polyurethane-Acrylate Hybrid Emulsion

Synthesis and Application of Hydroxyethyl Methacrylate Modified Waterborne Polyurethane

Synthesis and Characterization of High Performance Water Borne Polyurethane Emulsion

Synthesis and characterization of compound modification waterborne polyurethane

Preparation and Properties of Two-Component and Double-Crosslinking Waterborne Polyurethane-Acrylic Dispersions

Preparation and Characterization of Polyurethane-Acrylate Hybrid Emulsion

Synthesis and Characterization of Waterborne Polyurethane Dispersion with Low VOC Content and Low Film Forming Temperature

Study on preparation of aliphatic water-based hybrid emulsion of polyurethane-acrylate by multiple crosslink modification

Preparation and Characterization of a Self -Matting Coating Based on Waterborne Polyurethane-Polyacrylate Hybrid Dispersions

Factors Influencing Stability of PUA Hybrid Dispersion

Preparation, mechanical properties of waterborne polyurethane and crosslinked polyurethane‐acrylate composite

Synthesis of Waterborne Polyurethane-acrylate Adhesive for Laminated Film

Distribution of Hydrophilic Monomer Units and Its Effect on the Property of the Water Dispersion of Polyurethaneurea Anionomer

Synthesis of aqueous polyurethane modified by methyl methacrylate and butyl acrylate copolymer

Synthesis and Properties of Waterborne Polyurethane/ Acrylate Hybrid Dispersion with Excellent Flexibility at Low Temperature

Synthesis and Characterization of Ambient-Temperature Self-Crosslinked Waterborne Polyurethanes with a Novel Diol Chain Extender Bearing Two Ketone Groups

Synthesis and Characterization of Waterborne Polyurethane Adhesive from MDI and HDI

Preparation, properties and application of waterborne hydroxyl-functional polyurethane/acrylic emulsions in two-component coatings

Preparation, Thermal Property and Morphology Analysis of Waterborne Polyurethane-Acrylate

Synthesis and properties of high solid contents polyurethane-acrylate hybrid emulsions