Abstract:Aqueous polyurethane (PU) prepolymers were synthesized by emulsion polymerization in situ, with toluene diisocyanate (TD1-80), polyether binary alcohol (N210), dimethylol propionic acid (DMPA), hydroxyl ethyl methacrylate (HEMA), adipic dihydrazide (ADH) and diacetone acrylamide (DAAM) as the materials. Three kinds of aqueous polyurethane-acrylate (PUA) hybrid emulsions marked as PUA-1 (free cross-linking), PUA-2 (synthesized cross-linking) and PUA-3 (cross-linking at ambient temperature) were synthesized after the free radical polymerization by adding initiator, which were then used to prepare three kinds of varnishes. The effects of the dosages of DMPA, HEMA, ADH and DAAM on the properties of emulsions and films were finally investigated. It is found that, when the mass fraction of -COOH in DMPA and the mass fractions of HEMA, ADH and DAAM in PU are respectively 2.5%, 1.44%, 3.5% and 2.0%-3.0%, the emulsions and films are all of good properties. Moreover, the results obtained by particle size analyzer and TEM show that (1) the average particle sizes of PUA-1, PUA-2 and PUA-3 are respectively 40-50 nm, 90-100 nm and 30-40 nm; (2) PUA-1 particles are regular sphericities in shape, while PUA-2 particles are irregular sphericities with interpenetrating polymer network between the core and the shell; (3) as compared with PUA-1, PUA-2 is of larger particle size and wider particle size distribution; (4) PUA-3 is of very irregular particle shape, uniform particle size distribution and disorganized interpenetrating network between the shell and the core. Furthermore, in the three kinds of vanishes, the one prepared from PUA-3 is of the best water resistance, dry-heat resistance and stain resistance but is of the longest drying time for the film.

Synthesis and Characterization of High Performance Water Borne Polyurethane Emulsion

Synthesis and Characterization of Water-Borne Polyurethane-Acrylate Hybrid Emulsion

Factors affecting performance of polyurethane-acrylate hybrid emulsion

Synthesis and Application of Hydroxyethyl Methacrylate Modified Waterborne Polyurethane

Preparation and Properties of High Solid Content and Low Viscosity Waterborne Polyurethane—Acrylate Emulsion with a Reactive Emulsifier

Synthesis and characterization of compound modification waterborne polyurethane

Research of Synthesis and Properties Anionic Water-Borne Polyurethane Type Polyether Emulsion

Preparation, Characterization, and Property Analysis of Environmentally Friendly Waterborne Polyurethane-Acrylate

Preparation and characterization of waterborne polyurethane and its core-shell hybrid emulsions

Study on preparation of aliphatic water-based hybrid emulsion of polyurethane-acrylate by multiple crosslink modification

Preparation, properties and application of waterborne hydroxyl-functional polyurethane/acrylic emulsions in two-component coatings

Preparation and Characterization of Polyurethane-Acrylate Hybrid Emulsion

Factors of Influencing on Performances of UV-curable Waterborne Polyurethane-acrylate Emulsion

Synthesis and Characterization of Waterborne Polyurethane and its Composite

Preparation and Characterization of Polyol - Anionic Waterborne Polyurethane Adhesive

Synthesis of Waterborne Polyurethane Modified by Epoxy Resin and Acrylic Ester

Synthesis of Waterborne Polyurethane-acrylate Adhesive for Laminated Film

Synthesis and Performance of Acrylpimaric Acid Neopentyl Glyol Ester-Polycarbonate Diols Based Waterborne Polyurethane-Acrylate Hybrid Emulsion

Synthesis and properties of high solid contents polyurethane-acrylate hybrid emulsions

Synthesis Technology and Properties of Waterborne Polyurethane Modified by Epoxy Resin

Preparation, Thermal Property and Morphology Analysis of Waterborne Polyurethane-Acrylate