Abstract:The shift of the emission band to longer wavelength (yellow-orange) of the Ba2MgSi2−xAlxO7: 0.1Eu2+ phosphor under the 350–450nm excitation range has been achieved by adding the codoping element (Mn2+) in the host. The single-host silicate phosphor for WLED, Ba2MgSi2−xAlxO7: 0.1Eu2+, 0.1Mn2+ was prepared by high-temperature solid-state reaction. It was found experimentally that, its three-color emission peaks are situated at 623, 501 and 438nm, respectively, under excitation of 350–450nm irradiation. The emission peaks at 438 and 501nm originate from the transition 5d to 4f of Eu2+ ions that occupy the two Ba2+ sites in the crystal of Ba2MgSi2−x AlxO7, while the 623nm emission is attributed to the energy transfer from Eu2+ ions to Mn2+ ions. The white light can be obtained by mixing the three emission colors of blue (438nm), green (501nm) and red (623nm) in the single host. When the concentrations of the Al3+, Eu2+ and Mn2+ ions were 0.4, 0.1 and 0.1mol, respectively, the sample presented intense white emission. The addition of Al ion to the host leads to a substantial change of intensity ratio between blue and green emissions. White light could be obtained by combining this phosphor with 405nm light-emitting diodes. The near-ultraviolet GaN-based Ba2MgSi1.7 Al0.3O7: 0.1Eu2+, 0.1Mn2+ LED achieves good color rendering of over 85.

Energy Transfer in BaMgAl_(10)O_(17):(Eu~(2+),Mn~(2+) Phosphor

Energy Transfer Between Eu–Mn and Photoluminescence Properties of Ba0.75Al11O17.25–BaMgAl10O17:Eu2+,Mn2+ Solid Solution

BaMgAl10O17:Eu2+ Mn2+ Blue-Green Phosphor for White Light Emitting Diodes

Synthesis and luminous characteristics of Ba2MgSi2-xAlxO7: 0.1Eu2+, 0.1Mn2+ phosphor for WLED

Energy Transfer and Photoluminescence of BaMgAl10O17 Co-Doped with Eu2+ and Mn2+

Luminescence Properties and Energy Transfer of Ba2Mg(PO4)2:Eu2+, Mn2+ Phosphor Synthesized by Co-Precipitation Method

Luminescent properties of SrMgAl10 O17∶Eu2+,Mn2+ high-efficiency phosphor prepared via the sol-gel combustion method

Emission of BaMgAl_(10)O_(17):Eu~(2+) with High Concentration of Activator

Fluorescence Emission Spectrum and Energy Transfer in Eu and Mn Co-Doped Ba2Ca(BO3)2 Phosphors

Luminescent Properties of the BaMgAl10O17:Eu2+,M3+ (M = Nd, Er) Phosphor in the VUV Region

Luminescence of Ba0.85MgAl10O16.94 : EU0.092+ with different fluxes

Energy transfer mechanism and color-tunable luminescence properties of Eu3+-doped BaMg2V2O8 vanadate phosphors

Luminescence and Morphology of BaMgAl10O17:Eu2+ Phosphors Prepared from Different Phases of Al2O3

Photoluminescence Studies of Eu2+-Yb3+ Co-Doped BaMgAl10O17 Phosphor Synthesized by the Combustion Method

Luminescence of Ba0.85MgAl10O16.94:Eu 0.09 2+ with different fluxes

Luminescence of Ba 0.85 MgAl 10 O 16.94 :Eu 2+ 0.09 with Different Fluxes

Photoluminescence Properties of BaMgAl10O17:Eu2+ Phosphor Prepared by the Flux Method

The Luminescence of Eu3+ Activated Ba2mg(Bo3)(2) Phosphors

Luminescence properties of Eu2+ and Mn2+ Codoped 50SiO2-17Al2O3-23MgF2-10NaF glasses and glass-ceramics

Energy transfer from Eu2+ to Mn2+ in M 5(PO4)3Cl (M=Ca, Sr)

Effect of Er3+ and Nd3+ doping on the luminescent properties of BaMgAl10O17:Eu phosphor