Abstract:Calcium-phosphate cement (CPC) is currently used to treat bone defects; however, it may cause inflammation due to pH changes by an acid-base reaction during setting. Therefore, we have developed bioresorbable chelate-setting β-tricalcium phosphate (β-TCP) cement based on surface modification of inositol phosphate (IP6). In order to improve the bioresorbability, we have previously succeeded in preparing IP6/β-TCP cement hybridized with poly(lactic-co-glycolic acid) (PLGA) particles as a pore-forming agent. However, the hybrid cement had a prolonged setting time. In this study, calcium sulfate hemihydrate (CSH) was added to shorten the setting time and further improve the cement bioabsorbability, and the material properties of the resulting samples were clarified, together with an in vivo reaction. The cement setting time with the simultaneous addition of 10 mass% PLGA particles and CSH was successfully reduced from 26.3 min, the cement setting time without CSH addition, to 15 min; and the compressive strength of the cement exhibited 30 MPa or higher. The hard tissue compatibility of the resulting cement was qualitatively evaluated using a rat calvaria defect model. Subsequently, the bioresorption and bone formation rates of the cement were quantitatively determined using large animal pigs, which are more similar to humans in terms of their in vivo response. The highest bioabsorption (39.6%) and bone formation rates (24.2%) were confirmed for cement with the simultaneous addition of 10 mass% PLGA particles and CSH. Organic/inorganic hybrid cement with the simultaneous addition of CSH and PLGA particles is expected to be clinically applicable as a bone repair cement with a short setting time, improved compressive strength, and bioresorbability compatible with the bone remodeling cycle.

Setting Behavior of Fast-Setting Calcium Phosphate Cement with Mineral Phase of Bone

Self-Setting Biphase Porous Calcium Phosphate Cement

In Vivo Behavior of Injectable Fast-Setting Calcium Phosphate Cement

Research Progress on the Physicochemical Properties of Improved CPC

Mechanical and chemical properties of novel calcium-magnesium phosphate cements

Morphological and phase characterizations of retrieved calcium phosphate cement implants

In Vitro Primary Study of an Injectable and Fast Setting Calcium Phosphate Based Biomaterials

Preparation of CPC Carried by Eucommia Ulmoides Oliv. Extracts

Study on Cpc Carried by Rhbmp-2

In Vitro Primary Study Of An Injectable And Fast Setting Calcium Phosprate Based Biomaterials

Octacalcium phosphate phase forming cements as an injectable bone substitute materials: Preparation and in vitro structural study

Bioactive calcium sulfate/magnesium phosphate cement for bone substitute applications

The study of self-regulating α-TCP based composite by micro/nano scaled silk fibroin and α-CSH on physicochemical and biological properties of bone cement

Study on Physicochemical Properties of the Carbonated Hydroxyapatite Bone Cement

Structure, properties and animal study of a calcium phosphate/calcium sulfate composite cement

Effects of adding resorbable chitosan microspheres to calcium phosphate cements for bone regeneration

A type of injectable porous calcium phosphate cement in vivo

Characterization of a novel calcium phosphate/sulphate bone cement

Setting, hardening and resorption of calcium phosphate hydraulic cements

Compliance of an apatitic calcium phosphate cement with the short-term clinical requirements in bone surgery, orthopaedics and dentistry

Development of paste-like organic/inorganic artificial bones compatible with bone remodeling cycles, consisting of β-tricalcium phosphate, calcium sulfate hemihydrate, and poly(lactic-co-glycolic acid) particles